Microwave dielectric characteristics of NdAlO 3 -doped 0.95MgTiO 3 -0.05CaTiO 3 ceramics

Ji Liu,Chaowei Zhong,Yu Tao,Song Chen,Shuren Zhang

DOI: https://doi.org/10.1007/s10854-016-5606-y

2016-01-01

Abstract:The microwave dielectric properties and microstructures of 0.95MgTiO 3 –0.05CaTiO 3 ceramics with different amount of NdAlO 3 additions, prepared by the solid-state route, were investigated. It is found that doping of NdAlO 3 can significantly improve the density and dielectric properties of 0.95MgTiO 3 –0.05CaTiO 3 ceramic and the sintering temperature of 0.95MgTiO 3 –0.05CaTiO 3 ceramic can be lowed to 1275 °C. Microwave dielectric properties were correlated with the singtering temperature and the amount of NdAlO 3 additions. A maximum Q × f of 78000 GHz associated with an ε r of 20.94 and a τ f of −10.31 × 10 −6 /°C was achieved for the 5 wt% NdAlO 3 -doped 0.95MgTiO 3 –0.05CaTiO 3 ceramic sintered at 1275 °C/4 h.