Abstract:Nano-ZSM-5 with large amount and high strength of acid sites were successfully synthesized by hydrothermal crystallization of pure-silica nucleus in NaAlO2 alkali solution. The concentration of NaAlO2 alkali solution was decreased by increasing the H2O/Al ratio from 200 to 2600, which strongly determined the acidic properties and crystal size of the obtained nano-ZSM-5. Low concentration of NaAlO2 alkali solution was found unfavorable for the incorporation of Al into the bulk of ZSM-5 crystal in crystallization process. Hence, more Al distributed at the exterior of crystals, which enhanced the accessibility of the acid sites during reaction. Large amount and high strength of acid sites were produced for nano-ZSM-5 by increasing H2O/Al ratio. When the H2O/Al ratio increased from 200 to 2600, the total amount of acid sites increased from 0.59 to 0.81 mmol g(-1), much higher than conventional value of 0.50 mmol g(-1). In addition, the acid strength increased and the ratio of Bronsted/Lewis acid sites were sharply increased from 2.3 to 4.1 when the H2O/Al ratio increased. Moreover, the size of nano-crystal was also decreased by above decreasing the concentration of the NaAlO2 alkali solution. When the H2O/Al ratio was 2600, the obtained sample possessed total acid amount of 0.81 mmol g(-1) and crystal size of 60 nm, respectively. Methanol to hydrocarbon (MTH) reaction results showed that the increased acid sites of the catalyst decreased its catalytic lifetime to some extent, but the aromatics selectivity was tunable obviously. As for the catalyst prepared with H2O/Al ratio of 2000, the aromatics selectivity of the obtained catalyst reached to 66.0%. This paper provided a method for the fabrication of small-size nano-ZSM-5 with large amount and high strength of acid sites and regulated Al distribution for MTH reaction.

Molded MFI Nanocrystals As a Highly Active Catalyst in a Methanol-to-aromatics Process

ZSM-5 Crystals Grown on the Wall of a Long Tubular Reactor As a Structured Catalyst for Cracking of Endothermic Fuels

Preparation and Catalytic Properties of ZSM-5 Zeolite Films on FeCrAl Alloy Grids

Highly Dispersed CrOx Nanoparticle-Modified NaZSM-5 for Dehydration of Methanol to Dimethyl Ether

Constructing hierarchical ZSM-5 coated with small ZSM-5 crystals via oriented-attachment and in situ assembly for methanol-to-aromatics reaction

Bayberry-like ZnO/MFI Zeolite As High Performance Methanol-to-aromatics Catalyst.

Si/Al Ratio Induced Structure Evolution During Desilication-Recrystallization of Silicalite-1 to Synthesize Nano-Zsm-5 Catalyst for MTH Reaction

Controllable Synthesis of Nano-Zsm-5 Catalysts with Large Amount and High Strength of Acid Sites for Conversion of Methanol to Hydrocarbons

Methane Dehydro-aromatization over Mo/HZSM-5 in the Absence of Oxygen: A Multinuclear Solid-State NMR Study of the Interaction between Supported Mo Species and HZSM-5 Zeolite with Different Crystal Sizes

Highly Dispersed Crox Nanoparticles Modified Nazsm-5 for Lower Temperature Dehydration of Methanol to Dimethyl Ether

ZSM-5@MCM-41 core–shell composite with tunable shell thickness for n -heptane catalytic cracking reaction

In Situ Solid State NMR Observation of the Methanol-to-hydrocarbons (MTH) Process over Nanosized and Microsized HZSM-5 Zeolites

The influence of straight pore blockage on the selectivity of methanol to aromatics in nanosized Zn/ZSM-5: an atomic Cs-corrected STEM analysis study

Influence of framework Al distribution in HZSM-5 channels on catalytic performance in the methanol to propylene reaction

Enhanced catalytic performance of the hollow Mo/HZSM-5 nanocrystal for methane dehydroaromatization

Effects of the controllable mesostructure of nano-sized ZSM-5 on the co-cracking of phenolic bio-oil model compounds and ethanol

Size controllable synthesis of ZSM-5 zeolite and its catalytic performance in the reaction of methanol conversion to aromatics

Green synthesis of shaped nano-ZSM-5 toward more efficient methanol-to-hydrocarbon conversion

Crystal-plane Effects of MFI Zeolite in Catalytic Conversion of Methanol to Hydrocarbons

Preparation of nano ZSM-5 with hydrophobic surfaces and application to catalytic cracking of hydrocarbon fuels

Facile Creation of Hierarchical Nano-Sized ZSM-5 with a Large External Surface Area Via Desilication–recrystallization of Silicalite-1 for Conversion of Methanol to Hydrocarbons