Abstract:In this paper, an efficient route is developed for controllable synthesis of ordered mesoporous alumina (OMA) materials with variable pore architectures and high mesoporosity, as well as crystalline framework. The route is based on the nanocasting pathway with bimodal mesoporous carbon as the hard template. In contrast to conventional reports, we first realize the possibility of creating two ordered mesopore architectures by using a single carbon hard template obtained from organic-organic self-assembly, which is also the first time such carbon materials are adopted to replicate ordered mesoporous materials. The mesopore architecture and surface property of the carbon template are rationally designed in order to obtain ordered alumina mesostructures. We found that the key factors rely on the unique bimodal mesopore architecture and surface functionalization of the carbon hard template. Namely, the bimodal mesopores (2.3 and 5.9 nm) and the surface functionalities make it possible to selectively load alumina into the small mesopores dominantly and/or with a layer of alumina coated on the inner surface of the large primary mesopores with different thicknesses until full loading is achieved. Thus, OMA materials with variable pore architectures (similar and reverse mesostructures relative to the carbon template) and controllable mesoporosity in a wide range are achieved. Meanwhile, in situ ammonia hydrolysis for conversion of the metal precursor to its hydroxide is helpful for easy crystallization (as low as approximately 500 degrees C). Well-crystallized alumina frameworks composed of gamma-Al(2)O(3) nanocrystals with sizes of 6-7 nm are obtained after burning out the carbon template at 600 degrees C, which is advantageous over soft-templated aluminas. The effects of synthesis factors are demonstrated and discussed relative to control experiments. Furthermore, our method is versatile enough to be used for general synthesis of other important but difficult-to-synthesize mesoporous metal oxides, such as magnesium oxide. We believe that the fundamentals in this research will provide new insights for rational synthesis of ordered mesoporous materials.

Synthesis of Ordered Mesoporous Uranium Dioxide by A Nanocasting Route

Synthesis of Ordered Mesoporous U3O8 by a Nanocasting Route

Template-Free Synthesis and Mechanistic Study of Porous Three-Dimensional Hierarchical Uranium-Containing and Uranium Oxide Microspheres

One-Step Synthesis of Highly Ordered Mesoporous Silica Monoliths with Metal Oxide Nanocrystals in Their Channels

Self-assembled MOF Microspheres with Hierarchical Porous Structure for Efficient Uranium Adsorption

Synthesis of easily shaped ordered mesoporous titanium-containing silica

A Unique Transformation Route for Synthesis of Rodlike Hollow Mesoporous Silica Particles

Synthesis of Ordered Three-Dimensional Large-pore Mesoporous Silica and Its Replication to Ordered Nanoporous Carbon

Nanoporous arrays of metal sulfides templated by mesoporous silica

Synthesis of Highly Ordered Mesoporous Crystalline Ws2 and Mos2 Via A High-Temperature Reductive Sulfuration Route

Ordered Mesoporous Crystalline Gamma-Al2o3 with Variable Architecture and Porosity from a Single Hard Template.

Zeolite Crystallization Inside Chemically Recyclable Ordered Nanoporous Co3O4 Scaffold: Precise Replication and Accelerated Crystallization

Growth of Uranyl Hydroxide Nanowires and Nanotubes by the Electrodeposition Method and Their Transformation to One‐Dimensional U3O8 Nanostructures

One-step Synthesis of Hollow UO 2 Nanospheres Via Radiolytic Reduction of Ammonium Uranyl Tricarbonate

Synthesis of ordered mesoporous alumina with large pore sizes and hierarchical structure

Synthesis and catalytic advantage of a hierarchical ordered macroporous KIT-6 silica

Directional Growth and Reconstruction of Ultrafine Uranium Oxide Nanorods within Single-Walled Carbon Nanotubes

Bottom-up Construction of a Superstructure in a Porous Uranium-Organic Crystal.

A Facile Additive-Free Method for Tunable Fabrication of UO2 and U3O8 Nanoparticles in Aqueous Solution

Hydrothermal synthesis of UO2 nanoparticles and their formation mechanism

A facile dual-template-directed successive assembly approach to hollow multi-shell mesoporous metal–organic framework particles