Alkaline Oxidative Pressure Leaching of Arsenic and Antimony Bearing Dusts

Yuhu Li,Zhihong Liu,Qihou Li,Fupeng Liu,Zhiyong Liu
DOI: https://doi.org/10.1016/j.hydromet.2016.07.010
IF: 4.217
2016-01-01
Hydrometallurgy
Abstract:A new alkaline oxidative pressure leaching process was developed to remove arsenic from arsenic and antimony bearing dusts. The effect of NaOH concentration, oxygen partial pressure, temperature, liquid/solid ratio and reaction time on the leaching of arsenic, antimony and lead were investigated. It was found that >95% of arsenic was selectively leached using 40g/L NaOH with the oxygen partial pressure of 0.5MPa at a liquid/solid ratio of 10 and 140°C for 2h, while almost of antimony and lead remained in the residue. The complete separation of arsenic and antimony can be attributed to the oxidative transformation of arsenic and antimony. The low solubility sodium arsenite was completely oxidized to highly soluble sodium arsenate, while Sb2O3 was transformed into insoluble Sb3O6(OH) and NaSb(OH)6. In addition, the filtration performance of leach slurry was significantly improved due to reaction under hydrothermal conditions.
What problem does this paper attempt to address?