Abstract:This paper was aimed to investigate the hygrothermal effects on the mechanical behavior of the double lap shear joints of Carbon/Epoxy composite laminates, which were bonded using epoxy adhesive film SY14. First, experimental method was used to evaluate the hygrothermal dependent properties of the adhesive and the static response of composite laminate double lap joints at various environment conditions. The specimens were grouped into room temperature/dry (RD), room temperature/wet (RW), elevated temperature/dry (ED) and elevated temperature/wet (EW). The wet specimens were immersed in deionized water at temperature of 90 °C for 60 h and the elevated temperature is 95 °C. Tensile tests were carried out at room temperature and elevated temperature (95 °C) in a controlled chamber. Results showed that the elastic modulus and tensile strength decreased about 24% and 27% respectively after exposure to humidity environment. And a large degradation was found when exposure to high temperature while the plasticity became notable. The failure modes of the double lap shear joints were studied by visual inspection. It was found that both adhesive and cohesive failure happened for dry specimens at room temperature. While failure modes were dominated by cohesive failure after moisture exposure and adhesive failure at elevated temperature. Second, a finite element model was utilized to simulate the damage evolution of the double lap joints. The moisture diffusion process, swelling stress and thermal stress were included. And hygrothermal dependent cohesive law was considered to study the damage evolution. It revealed that failure modes were highly dependent on the weaker strength of adhesive and cohesive. Moisture absorption caused large degradation in cohesive strength, so the failure modes were mostly cohesive failure. Elevated temperature decreases strength of adhesive seriously, so adhesive failure dominates. Good agreement was achieved between the predicted failure loads and experimental results. And the predicted failure modes were also consistent with the experimental phenomenon.

Delamination analysis of carbon fiber composites under hygrothermal environment using acoustic emission

Delamination Analysis of Carbon Fiber/Epoxy Composite Laminates under Different Loading Rates Using Acoustic Emission

Identifying Delamination in Carbon Fiber Composites Based on Defect Modes in Imperfect Phononic Crystals

AE feature extraction and signal representation model based on wavelet packet decomposition

A Waveform Clustering Method for Damage Mode Identification for Composite Laminates under Hygrothermal Environment

Damage mode identification of adhesive composite joints under hygrothermal environment using acoustic emission and machine learning

A Study on the Failure Mechanisms of Carbon Fiber/epoxy Composite Laminates Using Acoustic Emission

A Study on the Intralaminar Damage and Interlaminar Delamination of Carbon Fiber Composite Laminates under Three-Point Bending Using Acoustic Emission

An Experimental Analysis for Damage Monitoring in Glass Fiber/Epoxy Composites During Fatigue Tests by Acoustic Emission

Study on Delamination Damage of CFRP Laminates Based on Acoustic Emission and Micro Visualization

Flexural progressive damage and failure behavior of carbon-aramid/epoxy hybrid woven composites

A New Quantitative Acoustic Emission Model for Damage Characterization of Composite Laminates Using Original Waveforms

Investigation on damage behaviors of carbon fiber‐reinforced nylon 6 thermoplastic composite laminates using acoustic emission and digital image correlation techniques

Dynamic Mechanical Analysis on Delaminated Flax Fiber Reinforced Composites

Static and dynamic diffuse wave inspection of delaminations in carbon fiber reinforced composites

Interlaminar Shear Properties and Acoustic Emission Monitoring of the Delaminated Composites for Wind Turbine Blades

Interlaminar Fracture Toughness Evaluation in Glass/Epoxy Composites Using Acoustic Emission and Finite Element Methods

Damage Localization, Identification and Evolution Studies during Quasi-Static Indentation of CFRP Composite Using Acoustic Emission

An investigation of hygrothermal effects on adhesive materials and double lap shear joints of CFRP composite laminates

Localization and characterization of delamination in laminates using the local wavenumber method

Detection of Acoustic Emission Signal Due to Impact Damage of Composite Materials Based EMD