Abstract:The development of high-speed aerial vehicles urgently requires high-performance integrated materials for ablation resistance, thermal insulation and oxidant protection under high temperature. The previously prepared carbon aerogel composites (C/CA), with ultra-high temperature thermal insulation properties, were impregnated with SiCO precursor sol and pyrolysed in nitrogen atmosphere at 1200?C. The impregnation/pyrolysis process was performed once, twice and thrice to obtain three different C/C-SiCO nanoporous ceramic composites. Further, TaSi2-MoSi2-borosilicate glass (TM-BG) coating or TaSi2-MoSi2-ZrB2-borosilicate glass (TMZBG) coating was prepared on the surface of the C/C-SiCO through slurry brushing combined with graphite powder embedded sintering process. By simulating the actual application environment through oxygen acetylene flame ablation test, the ablation resistance of the samples was studied and their oxidation mechanism was analysed. The results show that the ablation rate of the C/C-SiCO after 200 s ablation at 1600 ?C decreases with the increase of the number of impregnation/pyrolysis steps and that the ablation resistance of the coating modified C/C-SiCO was significantly enhanced. The addition of ZrB2 to the coating improves the compatibility between the substrates and the coating, and the TMZ-BG coated sample has better ablation resistance. At high temperature, the borosilicate glass in the coating is in a viscous flow state. Meanwhile the SiO2 generated by the oxidation of other silicide raw materials forms a dense glass layer on the coating surface, which can be used as an oxygen barrier to provide better protection for the substrates. The coating-modified C/C-SiCO porous ceramic composites are expected to be used as a high-temperature ablation-resistant material for the thermal protection system of new aerospace vehicles.

Ablation Behavior of TaB2SiC Coating for Carbon/carbon Composites under Oxyacetylene Torch

Effect of tantalum carbide on the ablation behaviors of hafnium carbide coating for C/C composites under single and cyclic oxyacetylene torch environments

Ablation behavior of Ta, TaC and Ta/TaC coatings on graphite under high-energy laser irradiation

TaSi2 modified HfB2‐SiC coating: preparation and ablation behavior

Ablation-resistance of ZrB2-SiC Coating under Oxygen-propane Torch Flame Prepared by Atmospheric Plasma Spraying

Ablation Mechanism of AlSiB-C/C Composites under an Oxy-Acetylene Torch

Preparation, Mechanical and Ablation Properties of a C/C-TaB2-SiC Composite

Ablation behavior and mechanisms of ZrC-SiC-MoSi2 coated C/C-SiC-ZrC ceramic matrix composites under oxyacetylene torch

Self‐defending mechanism of C/TaC‒SiC composites under 2100°C cyclic ablation environment

Ablation resistance of C/C-SiCo nanoporous ceramic composites with TaSi2-MoSi2-ZrB2-borosilicate glass coating

Ablation behaviour of the CVD-(ZrC/SiC)3 alternate coating on C/C composites under oxyacetylene torch with different heat fluxes

Ablation behavior of high-entropy boride (Hf-Zr-Ta-Ti)B 2 coating fabricated via supersonic atmospheric plasma spraying for carbon/carbon composites

Oxidation ablation resistance of ZrB2-HfB2-SiC-TaSi2 coating prepared on C/C composite surface

High-temperature oxidation and ablation behavior of plasma sprayed LaB6-MoSi2-TiB2 composite coating

Residual stress and ablation behavior of CVD TaC coatings on graphite

Ablation resistance of ZrB2SiC/SiC coating prepared by pack cementation for graphite

Cyclic ablation behavior and microstructure evolution of multi-layer coating on C/C composites under oxyacetylene torch

Cyclic ablation behavior of C/C–ZrC–SiC composites under oxyacetylene torch

Ultra-high Temperature Ceramic TaB2–TaC–SiC Coating for Oxidation Protection of SiC-coated Carbon/carbon Composites

Ablation-resistant Ta0.78Hf0.22C solid solution ceramic modified C/C composites for oxidizing environments over 2200 °C

Ablation resistance of SiC-modified nanocomposite ceramic coating prepared by LPDS method on titanium alloy