Enhanced dielectric properties and improved thermal stability in TiO 2 -based ceramics by Cu and Nb co-doping
Peng Qiao,Yingning Zhang,Jing Wang,Zhanhui Peng,Di Wu,Xiaolian Chao,Zupei Yang,Pengfei Liang
DOI: https://doi.org/10.1016/j.ceramint.2023.10.340
IF: 5.532
2023-12-04
Ceramics International
Abstract:TiO 2 -based ceramics have application potential in multilayer ceramic capacitors because of its large dielectric constant and low dielectric loss. In this work, Cu 2+ , Nb 5+ co-doped TiO 2 ceramics (CNTO) with colossal permittivity and low loss were designed and prepared via an oxide mixed method, and the effect of Cu 2+ , Nb 5+ co-doped amount on dielectric properties were systematically investigated. Remarkably, the compositions of (Cu 1/3 Nb 2/3 ) 0.005 Ti 0.995 O 2 and (Cu 1/3 Nb 2/3 ) 0.01 Ti 0.99 O 2 exhibit large dielectric permittivity ( ε r ) of ∼27,060 and ∼41,200 accompanied with low dielectric loss (tan δ) of ∼0.011 and ∼0.032 at 1 kHz, respectively. Based on dielectric properties, relaxation behavior assessments and X-ray photoelectron spectroscopy analysis, we confirmed that the high dielectric permittivity of CNTO ceramics mainly originates from the electron-pinned defect-dipole (EPDD) effect. Moreover, the temperature stability value of ε r keeps stable of ±7.5% at 1 kHz from −200 to 200 °C for (Cu 1/3 Nb 2/3 ) 0.005 Ti 0.995 O 2 and from 10 to 200 °C for (Cu 1/3 Nb 2/3 ) 0.01 Ti 0.99 O 2 ceramics, which separately meet the X9F and Z9F capacitor requirements, respectively. The findings presented in this work might have important strategic significance for promoting the miniaturization of electronic components.
materials science, ceramics