Phase Diagrams of Bi–Sb–Se–Te System
Sinn-wen Chen,Cheng-chun Ching,Yohanes Hutabalian,Chia-chun Chen
DOI: https://doi.org/10.1016/j.calphad.2023.102560
IF: 2.004
2023-01-01
Calphad
Abstract:Bi-Sb-Se-Te is one of the most important material systems for thermoelectric applications. Phase diagrams of its constituent binary and ternary systems are reviewed and assessed. The Bi-Sb-Se-Te isothermal section tetrahedron at 400 degrees C and liquidus projection tetrahedron were proposed. Ternary compounds are only found in the Bi-Sb-Se system. There are eight three-phase regions at 400 degrees C and seven primary solidification phases in the Bi-Sb-Se system, including (Bi,Sb), (Bi2)m(Bi2Se3)n, Bi2Se3, Se, Sb2Se3, Bi3Sb5Se2, Bi3Sb12Se15. In the Bi-Sb-Te system, there are four three-phase regions at 400 degrees C. The (Bi,Sb)2Te3 and (Bi,Sb) are continuous solid solutions. There are six primary solidification phases, including (Bi,Sb)2Te3, (Te), gamma, 8, (Bi,Sb), and (Bi2)m(Bi2Te3)n. In the Bi-Se-Te system, there is one three-phase region. (Bi2)m(Bi2Se3)n and (Bi2)m(Bi2Te3)n form a continuous solid solution phase at 400 degrees C. There are four primary solidification phases, including Bi, (Bi2)m(Bi2(Se,Te)3)n, Bi2(Se, Te)3 and (Se,Te). In the Sb-Se-Te system, there are five three-phase regions and six primary solidification phases, including (Sb), 8-(Sb2Te), gamma-(SbTe), Sb2Te3, and (Se,Te). A wide range of (Bi,Sb)2(Se,Te)3 single-phase region was observed in the Bi-Sb-Se-Te quaternary system.