Abstract:Honeycomb sandwich panels are utilized in many industrial applications due to their high bending resistance relative to their weight. Defects between the core and the facesheet compromise their integrity and efficiency due to the inability to transfer loads. The material system studied in the present paper is a unidirectional carbon fiber composite facesheet with a honeycomb core with a variety of defects at the interface between the two material systems. Current nondestructive techniques focus on defect detectability, whereas the presented method uses high-frequency ultrasound testing (UT) to detect and quantify the defect geometry and defect type. Testing is performed using two approaches, a laboratory scale immersion tank and a novel portable UT system, both of which utilize only single-side access to the part. Coupons are presented with defects spanning from 5 to 40 mm in diameter, whereas defects in the range of 15–25 mm and smaller are considered below the detectability limits of existing inspection methods. Defect types studied include missing adhesive, unintentional foreign objects that occur during the manufacturing process, damaged core, and removed core sections. An algorithm is presented to quantify the defect perimeter. The provided results demonstrate successful defect detection, with an average defect diameter error of 0.6 mm across all coupons studied in the immersion system and 1.1 mm for the portable system. The best accuracy comes from the missing adhesive coupons, with an average error of 0.3 mm. Conversely, the worst results come from the missing or damaged honeycomb coupons, with an error average of 0.7 mm, well below the standard detectability levels of 15–25 mm.

Near-field Microwave Identification and Quantitative Evaluation of Liquid Ingress in Honeycomb Sandwich Structures

In situ near-field microwave characterization and quantitative evaluation of phase change inclusion in honeycomb composites

MmLiquid: Liquid Identification Using Mmwave.

Multisection Step-Impedance Modeling and Analysis of Broadband Microwave Honeycomb Absorbing Structures

A novel nondestructive testing method for honeycomb structure using acoustic band gap

Nondestructive In-situ Permittivity Measurement of Liquid Within a Bottle Using an Open-Ended Microwave Waveguide

Microwave Nondestructive Detection of Delamination in IC Packages Utilizing Open-Ended Coaxial Line Sensor

Defect detection of GFRP/Nomex honeycomb sandwich structure by linear frequency modulation infrared thermal imaging

Nondestructive Inspection and Quantification of Select Interface Defects in Honeycomb Sandwich Panels

Numerical and experimental investigation on debonding detection in honeycomb sandwich using air-coupled local defect resonance and coda wave analysis

Damage Imaging Identification of Honeycomb Sandwich Structures Based on Lamb Waves

A high-efficiency nondestructive method for remote detection and quantitative evaluation of pipe wall thinning using microwaves

G0310501 A Method for Quantitative Evaluation of Pipe Wall Thinning Using Microwaves

Detection of delamination in IC packages using the phase of microwaves

Evaluating Water Ingress in Glass Fiber Plastic/Nomex Honeycomb Panels under Varying Panel Orientation

Microwave Measurement and Quantitative Evaluation of Wall Thinning in Metal Pipes

Sandwich nanoarchitectonics of heterogenous CB/CNTs honeycomb composite for impedance matching design and microwave absorption

Investigation of the pore-size dependent microwave absorption properties of honeycomb SnO2

Enhanced Microwave-Absorbing Property of Honeycomb Sandwich Structure with a Significant Interface Effect

Microwave Near-Field Detection of the Ion Concentration in Sealed Fluidic Systems

A Resonant Microwave Patch Sensor for Detection of Layer Thickness or Permittivity Variations in Multilayered Dielectric Structures