Abstract:Al/Mg/Al sheet with good bonding quality and mechanical properties was fabricated based on the proposed porthole die co-extrusion and forging (PCE-F) process. There were no voids, cracks or other defects on the Al/Mg interface. A continuous diffusion zone with two-sub-layer structure was formed across the Al/Mg interface, and its width increased with higher temperature or reduction ratio. The sub-layers formed at low and high temperature were identified to be solid solutions and intermetallic compounds (IMCs) including γ-Mg17Al12 and β-Al3Mg. In Al layer, the welding zone mainly consisted of fine equiaxed grains with several coarse elongated grains, while the majority of matrix zone is coarse elongated grains. The rolling textures were dominated in both welding and matrix zones. In Mg layer, the welding zone exhibited complete DRXed grain structure, while several unDRXed coarse grains were observed in the matrix zone. With the increasing temperature, the grain size of Al and Mg layer firstly decreased and then increased. High reduction ratio strongly refined the grain structure of Al layer, while slightly affected the Mg layer. The Al/Mg/Al sheet experienced stress-drops twice during the tensile test. The first stress-drop was determined by the IMCs and microstructure of Mg layer, while the second stress-drop was closely related to the microstructure of Al layer. Al/Mg/Al sheet forged at the lowest temperature without the formation IMCs exhibited the highest stress for the first stress-drop, and that forged under the highest reduction ratio with the smallest grain size in Al layer had the highest stress for the second stress-drop.

Intermetallics Formed at Interface of Ultrafine Grained Al/Mg Bi-Layered Disks Processed by High Pressure Torsion at Room Temperature

Fabrication of Ultrafine Grained Al/Mg Multilayered Composite by High Pressure Torsion

Quasicrystal phase evolution and mechanical properties of Mg-3.5Zn-0.6Gd alloy processed by high-pressure torsion

Microstructural Evolution and Mechanical Properties in Superlight Mg-Li Alloy Processed by High-Pressure Torsion

Evolution of Microstructure and Mechanical Properties of an As-Cast Mg-8.2gd-3.8y-1.0zn-0.4zr Alloy Processed by High Pressure Torsion

Fabrication and Interface Structural Behavior of Mg/Al Thickness-Oriented Bonding Sheet via Direct Extrusion

Achieving three-layered Al/Mg/Al sheet via combining porthole die co-extrusion and hot forging

Analysis of Heterogeneities in Strain and Microstructure in Aluminum Alloy and Magnesium Processed by High-Pressure Torsion

The effect of high-pressure torsion on the behaviour of intermetallic particles present in Al–1Mg and Al–3Mg

Characterisation of precipitates formed in high-pressure torsion treated Mg-3.4at.%Zn alloy

Microstructure and Mechanical Properties of Al-4Mg-0.3Cu Alloy after HPT and Postdeformation Annealing

Microstructure and Mechanical Properties of a Nanostructured Mg-8.2Gd-3.8Y-1.0Zn-0.4Zr Supersaturated Solid Solution Prepared by High Pressure Torsion

Microstructure Evolution during High-Pressure Torsion in a 7xxx AlZnMgZr Alloy

The nanoscale mechanisms of strengthening and ductility enhancement in an Al–Mg–Si–Mn alloy on processing by high-pressure torsion

Microstructures and Properties of AlMgTi-Based Metal-Intermetallic Laminate Composites by Dual-Steps Vacuum Hot Pressing

Phase Transformation in Al/Zn Multilayers during Mechanical Alloying

Micro‐Embossing Formability of a Superlight Dual‐Phase Mg–Li Alloy Processed by High‐Pressure Torsion

Coherent interface strengthening of ultrahigh pressure heat-treated Mg-Li-Y alloys

Hardening Mechanism of Commercially Pure Mg Processed by High Pressure Torsion at Room Temperature

Design, fabrication, microstructure, and mechanical properties of interlayer-free vacuum diffusion bonding Mg/Ti composites

Effect of Bimodal Quasicrystal Phase on the Dynamic Recrystallization of Mg–Zn–Gd Alloy during High-Pressure Torsion