Abstract:Polyurethane-cement composite are widely used in modern civil engineering, and the method of adding diluent is often used to adjust the construction process to adapt to the engineering environment. Studies have shown that the addition of diluent impacts the performance of polyurethane-cement based composite surface coatings, but there have been few reports on the influence of diluent content on the mechanical properties and microstructure of the coatings. To address this, polyurethane coatings with different diluent contents were prepared, and positron annihilation lifetime spectroscopy was used to test the microstructure of the coatings. The tensile strength and elongation at rupture were tested using a universal material testing machine, and the fracture interface morphology of each coating was observed by scanning electron microscopy. Finally, the correlation between the microstructure parameters and the mechanical properties of the coating was analyzed using grey relation theory. The results demonstrated that with the increase in diluent content, (i) the average radius of the free volume hole (R) and the free volume fraction (FV) of the coating both showed a trend of first decreasing and then increasing. The value of R was between 3.04 and 3.24 Å, and the value of FV was between 2.08 and 2.84%. (ii) The tensile strength of the coating increased first and then decreased, while the elongation at rupture decreased first and then increased. Among them, the value of tensile strength was between 3.23 and 4.02 MPa, and the value of elongation at fracture was between 49.34 and 63.04%. In addition, the free volume in polymers plays a crucial role in facilitating the migration of molecular chain segments and is closely related to the macroscopic mechanical properties of polymers. A correlation analysis showed that the R value of the coating had the greatest influence on its tensile strength, while FV showed a higher correlation with the elongation at rupture.

A STUDY OF DILUTE SOLUTION BEHAVIOR OF POLYURETHANE

Distribution of Hydrophilic Monomer Units and Its Effect on the Property of the Water Dispersion of Polyurethaneurea Anionomer

THE STUDY OF BEHAVIOR OF POLYURETHANE MICROGELS IN DILUTE SOLUTION

Synthesis of soluble polyurethaneurea microgels and measurement of their molecular dimension

Studies on the influence of soft-segment structure on the properties of polyurethane adhesive

Various Nanoparticle Morphologies and Surface Properties of Waterborne Polyurethane Controlled by Water.

Structural analysis and property of aqueous polyurethane dispersion

Influence of Dilution on the Mechanical Properties and Microstructure of Polyurethane-Cement Based Composite Surface Coating

Synthesis and performance study on water-borne polycarbonate-based PU dispersion

Special Solution Behavior of Soluble Intramolecularly Cross-Linked Macromolecule of Polyurethane with A Hexaethylene Diamine Chain Extender

The Design, Synthesis And Characterization Of Polyurethane With Super Macromolecular Size

Spectroscopic Analysis of Ordering and Phase-Separation Behavior of Model Polyurethanes in a Restricted Geometry

Synthesis and Charactenization of High Solid Polyurethane Dispersion Based on Amino - sulfonate and TDI

Dynamic mechanical analysis of sulfonated polyurethane ionomers

Protean Morphology of Waterborne Polyurethane Dispersion: an Overview of Nanoparticles from Sphere to Irregular Elongated Shape

Synthesis of High Solid Content Aqueous Polyurethane and Study on Properties of Filming

Monte Carlo Simulation Of Single Chain Of High Performance Polymer.

Study of water-borne polyurethane ( I )

Preparation and Size Determination of Soluble Cross-Linked Macromolecule of Polyurethane

VISCOSITY STUDIES ON THE SOLUTION BEHAVIOR OF SOLUBLE POLYURETHANE INTROMOLECULARLY CROSS-LINKED MACROMOLECULES

Influence of dangling chains on the microphase separation and damping properties of polyurethane