Synthesis and properties novel polyurethane-hexafluorobutyl methacrylate copolymers

Guichang Jiang,Xinlin Tuo,Dongrui Wang,Qiang Li

DOI: https://doi.org/10.1007/s10856-012-4670-y

2012-01-01

Abstract:Novel physically crosslinked polyurethane-hexafluorobutyl methacrylate (PU-M) copolymers were prepared by the macroiniferter-controlled radical polymerization method. The chemical structures of the PU-M copolymers were characterized by FT-IR, 1 H-NMR, GPC, DSC, and XPS. The self-assembly and surface properties of the PU-M copolymers have been investigated. The results revealed that PU-M copolymers have good hydrophobility, so the hydrophobility of polyurethane could be easily adjusted by controlling the content of the hydrophobic vinyl monomers. The mechanical evaluation shows that PU-M copolymers exhibit good mechanical properties. The effects of the fluorine content on the surface properties and self-assembly of the PU-M copolymers were investigated. The morphology of the PU-M copolymers’ self-assembly was observed by transmission electron microscopy (TEM) and scanning electron microscopy (SEM), and the mechanism of self-assembly was investigated. Antimicrobial property of the chlorinated PU-M copolymers against both Escherichia coli and Bacillus subtilis bacteria was examined and showed increase compared to that of pure polyurethane. Graphical Abstract Novel PU-M copolymers were synthesized by the macroiniferter controlled radical polymerization method. The structure of polymers was characterized by 1 H NMR and IR. Solvent-induced assembly of polymers was investigated by dissolving the polymer in THF:water (80:20, v/v), filtering and dropping onto a glass patch. After evaporation for 48 h under ambient conditions, the samples were observed by SEM. The PU-M copolymers were subjected to solvent-induced self-assembly in THF + water to construct variety of morphologies ranging from pores (150–650 nm) to spheres (90 nm to 1.2 μm). A mechanism is proposed according to solvent-induced self-assembly.