Spectroscopic Analysis of Ordering and Phase-Separation Behavior of Model Polyurethanes in a Restricted Geometry

CW MEUSE,XZ YANG,DC YANG,SL HSU

DOI: https://doi.org/10.1021/ma00028a064

IF: 5.5

1992-01-01

Macromolecules

Abstract:Ultrathin films (40-300 angstrom) of model polyurethanes with monodisperse hard segments were studied as a function of film thickness and sample preparation. External-reflection infrared spectroscopy incorporating the double-modulation technique was used to characterize the phase-separation behavior of these copolymers into hard-segment-rich or soft-segment-rich domains. Using the C = O stretching or N-H in-plane-bending vibrations, vibrational spectroscopy can independently probe the localized hydrogen-bonding environment and the orientation of the hard segments in both domains. For anisotropic ultrathin films studied by reflection spectroscopy, the band intensities observed represent the degree of phase separation as well as the orientation of the urethane groups on the substrate. A procedure was developed to separate effects arising in phase separation from those related to segmental orientation. On solid surfaces, the results indicate that the amount of orientation and degree of phase separation observed is controlled by the film thickness. Annealing studies reveal that the reduced mobility of the polyurethanes on the surface prevents the thin films from achieving degrees of phase separation similar to those observed in the bulk. Glycerin is expected to have a specific interaction with the polyurethane, and the microstructure of a thin polyurethane film cast on a glycerin surface is different from that of thin films cast on gold. The increased mobility of polyurethanes on glycerin allows a higher degree of phase separation to be achieved. In addition, upon annealing on the surface of glycerin, transmission electron microscopy reveals changes in aggregation of the hard domains, while spectroscopy shows orientation changes.