Abstract:In this study, the leaching kinetics of manganese oxide powder supplied from spent alkaline batteries was investigated in H2SO4 solutions including molasses. Waste battery powder containing manganese oxides was prepared by separating manually from the other components of the collected waste alkaline batteries. The leaching experiments were carried out in a batch reactor. The effects of H2SO4 concentration, stirring speed, solid-to-liquid ratio, reaction temperature, particle size, and amount of molasses on the leaching rate of manganese were studied. It was determined that molasses used as the reducing agent had an important effect on the leaching rate. By adding molasses to the leaching media, it was found that almost all manganese in waste battery powder transferred to the solution. It was observed that the leaching rate increased with an increase in the solution concentration, stirring speed, reaction temperature, and amount of molasses, and with a decrease in the particle size and solid-to-liquid ratio. While the concentration of H2SO4, stirring speed, solid-to-liquid ratio, reaction temperature, particle size, amount of molasses, and reaction time were 1 M, 500 rpm, 2/500 g/mL, 60 °C, 0.348 mm, 2 g, and 120 min, respectively, the amount of the dissolved manganese was found to be approximately 98%. A mathematical model represented that the leaching kinetics was elaborated. It was determined that the leaching kinetics followed the mixed kinetic model. The activation energy value for the process was calculated to be 52.31 kJ/mol. After the leaching treatment, Mn (II) ions in the solution were recovered in the form of MnCO3 using NaHCO3 solution. MnCO3 was calcined isothermally at 400 °C for 4 h, and MnO2 was produced.Graphical Abstract

Selective Leaching of Zinc From Waste Alkaline Batteries Using Sulfuric Acid

Studies of Selective Recovery of Zinc and Manganese from Alkaline Batteries Scrap by Leaching and Precipitation

Research on Pre-separation of Zn from Spent Zinc-manganese-carbon Batteries Cathode Material

Bioleaching of Zinc and Manganese from Spent Zn-Mn Batteries and Mechanism Exploration.

Advances in the Sustainable Production of Fertilizers from Spent Zinc-Based Batteries

A Novel Procedure for Comprehensive Recovery of Zinc Fluoride, Manganese Fluorides, Manganese Dioxide, and Carbon Powder from the Electrode Powder of Spent Alkaline Batteries

Study of Spent Battery Material Leaching Process

Leaching Kinetics of Manganese Oxides Obtained from Waste Alkaline Batteries in Sulfuric Acid Solutions Containing Molasses

Reclaiming the spent alkaline zinc manganese dioxide batteries collected from the manufacturers to prepare valuable electrolytic zinc and LiNi0.5Mn1.5O4 materials

Study of the factors influencing the metals solubilisation from a mixture of waste batteries by response surface methodology

Selective Lithium Recovery from Spent Lithium Manganate Batteries Using Oxidative Stabilization Technique

Extraction of Valuable Metals from Waste Battery Material

Extraction and separation of potassium, zinc and manganese issued from spent alkaline batteries by a three‐unit hydrometallurgical process

Study of Extraction and Purification of Ni, Co and Mn from Spent Battery Material

A critical updated review of the hydrometallurgical routes for recycling zinc and manganese from spent zinc-based batteries

Electrochemical processing of the active mass of spent manganese-zinc chemical current sources

Leaching Behavior Analysis of Valuable Metals from Lithium-Ion Batteries Cathode Material

Recycling of Valuable Metals from the Priority Lithium Extraction Residue Obtained through Hydrogen Reduction of Spent Lithium Batteries

Recycling of zinc‐carbon batteries into MnO/ZnO/C: a smart strategy to fabricate sustainable cathode for rechargeable zinc ion batteries

Alkaline Leaching and Concurrent Cementation of Dissolved Pb and Zn from Zinc Plant Leach Residues

Selective dissolution and kinetics of leaching zinc from lime treated electric arc furnace dust by alkaline media