Abstract:A comparative evaluation of the low-cycle fatigue (LCF) behavior of type 316LN base metal, 316 weld metal, and 316LN/316 weld joints was carried out at 773 and 873 K. Total strain-controlled LCF tests were conducted at a constant strain rate of 3 × 10−3 s−1 with strain amplitudes in the range ±0.20 to ±1.0 pct. Weld pads with single V and double V configuration were prepared by the shielded metal-arc welding (SMAW) process using 316 electrodes for weld-metal and weld-joint specimens. Optical microscopy, scanning electron microscopy (SEM), and transmission electron microscopy (TEM) of the untested and tested samples were carried out to elucidate the deformation and the fracture behavior. The cyclic stress response of the base metal shows a very rapid hardening to a maximum stress followed by a saturated stress response. Weld metal undergoes a relatively short initial hardening followed by a gradual softening regime. Weld joints exhibit an initial hardening and a subsequent softening regime at all strain amplitudes, except at low strain amplitudes where a saturation regime is noticed. The initial hardening observed in base metal has been attributed to interaction between dislocations and solute atoms/complexes and cyclic saturation to saturation in the number density of slip bands. From TEM, the cyclic softening in weld metal was ascribed to the annihilation of dislocations during LCF. Type 316LN base metal exhibits better fatigue resistance than weld metal at 773 K, whereas the reverse holds true at 873 K. The weld joint shows the lowest life at both temperatures. The better fatigue resistance of weld metal is related to the brittle transformed delta ferrite structure and the high density of dislocations at the interface, which inhibits the growth rate of cracks by deflecting the crack path. The lower fatigue endurance of the weld joint was ascribed to the shortening of the crack initiation phase caused by surface intergranular crack initiation and to the poor crack propagation resistance of the coarse-grained region in the heat-affected zone.

LOW CYCLE FATIGUE OF 14mnnbq STEEL WELDED JOINTS

Low Cycle Fatigue Properties and Fracture Mechanism of Q345qC Steel and Its Welded Joint

Fatigue Testing in Welded Joint of 980- grade Steels

Use of instrumented indentation testing to study local mechanical properties of 304L SS welded joints subjected to low-cycle fatigue loadings

Experimental and Numerical Characterization of Low Cycle Fatigue and Creep Fatigue Behaviour of P92 Steel Welded Joint

Some issues of fatigue failure of welded structures

Low-Cycle Fatigue Behaviour of Stainless-Clad Bimetallic Steel Welded Connections

Study on Fatigue Behavior and Crack Propagation Life of Longitudinal Fillet Welded Lap Joint

High-Cycle, Low-Cycle, Extremely Low-Cycle Fatigue and Monotonic Fracture Behaviors of Low-Carbon Steel and Its Welded Joint

Influence of Element Segregation at Grain Boundary of Heat Affected Zone on Low-cycle Fatigue Property of Weldment

Low-cycle fatigue in ultra-high-strength steel welded joints in the as-welded and post-weld-treated conditions

Ultra-Low Cyclic Fatigue Fracture of Q235B and Q345B Steels and Their Butt Welded Joints

Low cycle fatigue analysis of welded joints considering material cycling behavior

A comparative evaluation of low-cycle fatigue behavior of type 316LN base metal, 316 weld metal, and 316LN/316 weld joint

Fatigue Behavior of Low Alloy Structural Steel Single-Lap Bolt-Welded Joint

Ultra-high Cycle Fatigue Behaviors of Q345 Bridge Steel Welded Joint

Study of Microstructure and Fatigue in Aluminum/Steel Butt Joints Made by CMT Fusion-Brazing Technology

Mechanisms Affecting the Difference in Fatigue Resistance Between Welds and Base Materials Were Investigated Based on In-Situ Fatigue Method

Fatigue of Friction Stir Welded Aluminum Alloy Joints: A Review

Study on high-cycle fatigue properties of 9 %Ni steel joints welded by GTAW and SAW using nickel-based alloy