Behavior of SiO2 in the Precipitation of Caustic Aluminate Solutions
LIANG Cheng,CHEN Qi-yuan,LI Jie,YIN Zhou-lan
DOI: https://doi.org/10.3969/j.issn.1007-7545.2007.05.004
2007-01-01
Abstract:The behavior of SiO2 in the precipitation of Gibbsite in caustic aluminate solution has been investigated by ion membrane electrolysis.The microstructure of unseeded precipitation of aluminum hydroxide and its surface elements were characterized by using scanning electronic microscope(SEM) and Electron Spectrometer.The results show that silicon dioxide influenced on precipitated process obviously.The concentration change of SiO2 upon 0.60 g/L in the precipitation process was thought to be undertaken there-step: decrease quickly at first,a lag period step secondly and a slow step thirdly.The precipitation ratio are up to 50% after six hours in pure solution or sodium aluminate solution with SiO2.The precipitation rate was faster at 70℃ comparing with 60℃,especially at the first hour its precipitation ration almost 40%,which indicates that the decomposition of supersaturated sodium aluminate solution is controlled by chemical reaction.The number of particle size under 10 μm was increased in the present of SiO2,and the effecting of SiO2 on the number of fine particle size at 60℃ was more than at 70℃.The SEM present that the surface of Al(OH)3 from unseeded precipitated pure solution were lubricity,but there were some fine particle size in the surface of Al(OH)3 from solutions with SiO2,especially some foreign colloid-like crystal was appeared.In colloid area,four elements (Si,Al,O and Na) was detected by Electron Spectrometer,it is speculated that sodium aluminum silicate may be exist.