Abstract:The precipitation of spherical boehmite was studied by surface energy calculations, measurements of precipitation ratios, Fourier transform infrared spectroscopy, X-ray diffraction, scanning electron microscopy, and transmission electron microscopy. The surface energy calculation results show that the (001) and (112) planes of gibbsite surfaces are remarkably stable because of their low surface energies. In addition, the (010) plane of boehmite grows preferentially during precipitation because of its low surface energy. Thus, we propose a method to precipitate spherical boehmite from a supersaturated sodium aluminate solution by adding gibbsite as seed in a heterogeneous system. In this method, gibbsite acts as the preliminary seed and saturation modifier. The results show that the fine boehmite first nucleates on the (001) and (112) planes of gibbsite and then grows vertically on the (001) and (112) basal planes of gibbsite via self-assembly, thereby forming spherical boehmite. Simultaneously, gibbsite is dissolved into the aluminate solution to maintain the saturation for the precipitation of boehmite. The precipitation ratio fluctuates (forming an M-shaped curve) because of gibbsite dissolution and boehmite precipitation. The mechanism of boehmite precipitation was further discussed on the basis of the differences in surface energy and solubility between gibbsite and boehmite. This study provides an environmentally friendly and economical method to prepare specific boehmite in a heterogeneous system.

Concentration Variation of Aluminate Ions During the Seeded Precipitation Process of Gibbsite from Sodium Aluminate Solution

Intensifying Gibbsite Precipitation from Sodium Aluminate Solution by Adding a Mixed Seed

Enhanced Precipitation of Gibbsite from Sodium Aluminate Solution by Adding Agglomerated Active Al(OH)3 Seed

SEM Observation of Gibbsite Precipitation with Seeds from Sodium Aluminate Solutions Promoted by Ultrasound

Behavior of SiO2 in the Precipitation of Caustic Aluminate Solutions

Precipitation of Spherical Boehmite from Concentrated Sodium Aluminate Solution by Adding Gibbsite As Seed

Phenomena in Late Period of Seeded Precipitation of Sodium Aluminate Solution

Increasing Precipitation Rate from Sodium Aluminate Solution by Adding Active Seed and Ammonia

Precipitation Rate and Particle Size Distribution of Seeded Precipitation Proceeding in Sodium and Potassium Aluminate Solutions

Transformation of Monomer Aluminate Ions from Tetrahedron to Octaheron

Intensification of precipitation of gibbsite from seeded caustic sodium aluminate liquor by seed activation and addition of crown ether

Kinetics of Crystal Growth on Seeded Precipitation of Sodium Aluminate Solutions with New Device

Kinetics of super-fine aluminum hydroxide precipitation from sodium aluminate solutions with gel-seed

Nucleation During Gibbsites Precipitation with Seeds from Sodium Aluminate Solution Processed under Ultrasound

Effect of α-alanine on the seeded precipitation of sodium aluminate solution

Effect of Lithium Ion on Seed Precipitation from Sodium Aluminate Solution

Effect of mechanically activated seeds on the agglomeration process of supersaturated sodium aluminate liquors

Effect of silicon-containing impurity on precipitation of sodium aluminate solution and interaction mechanism

Continuous changes in electrical conductivity of sodium aluminate solution in seeded precipitation

Effects of Temperature and Initial Molar Ratio of Na 2 O to Al 2 O 3 on Agglomeration of Fine Al(OH) 3 Seed in Synthetic Bayer Solution

Thermodynamic Properties of Depositing Alumina Hydrate from Sodium Aluminate Solutions