Abstract:In this research, the electrochemical properties of a stir cast Al-0.65Mg-0.15Sn-0.05Ga (wt.%) alloy as an anode material in 3 wt.% NaCl solution was examined by potentiodynamic polarization and electrochemical impedance spectroscopy (EIS). The corrosion behavior of the material was also evaluated using self-corrosion rate, hydrogen evolution, open circuit and closed circuit potentials, and anode efficiency measurements. In addition, the microstructure of the material was studied using scanning electron microscopy (SEM) and the intermetallic particles were analyzed by energy dispersive spectrometer (EDS). The results showed that tin inclusions were formed within the grains and along the grain boundaries and the dissolution of aluminum substrate was occurred preferentially around these particles leading to form round pits. The dissolution of alloy was accompanied by hydrogen gas evolution from cathodic tin particles. Polarization measurements showed active behavior with considerably negative corrosion potential value without any passive region. The obtained impedance results showed an increase in the impedance values due to the coverage of anode surface by reaction products during immersion. A sample of the alloy which was subjected to homogenizing annealing at 570 °C showed more active behavior by providing more negative open and closed circuit potential values and improved anode efficiencies at higher impressed currents, but evolved higher amounts of hydrogen compared to the as-cast anode.Graphical abstractThis paper aims at evaluating the electrochemical and microstructural characteristics of an as-cast and solution-annealed Al-0.65Mg-0.15Sn-0.05Ga alloy anode which was fabricated by stir casting. The polarization and EIS results indicate negative corrosion potential and OCP values without passive region. The activity and anodic efficiency of the solution-annealed anode was higher in high impressed current densities but evolves more hydrogen

Electrochemical Behavior of Anodes Based on Al-In-Mg Alloys in NaOH Solution

Electrochemical Performance of Pure Al, Al–Sn, Al–Mg and Al–Mg–Sn Anodes for Al-air Batteries

Electrochemical Performance of Melt-Spinning Al–Mg–Sn Based Anode Alloys

Effects of Alloying Elements on Electrochemical Performance of Aluminum Anodes

Electrochemical Performances of Al–0.5Mg–0.1Sn–0.02In Alloy in Different Solutions for Al–air Battery

Effects of Electrolyte Additives on Behavior of Al-In-Ga-Pb Alloy Anode

The Anodic Behavior of Al-alloy in Alkine and Neutral Solution

Corrosion and Discharge Behaviors of Al-Mg-Sn-Ga-In in Different Solutions

Establishment of electrode potential-composition plot of Al-Mg-Zn alloys and sacrificial anode protection tests

Corrosion and Anodic Behaviors of Pure Aluminum in a Novel Alkaline Electrolyte

Effects of Alloying Elements on the Electrochemical Behaviors of Al-Mg-Ga-In Based Anode Alloys

Effects of Al and Sn on Electrochemical Properties of Mg-6%Al-1%Sn （mass Fraction） Magnesium Alloy As Anode in 3.5%nacl Solution

Electrochemical Behavior of Mg-Al-Pb Alloy in 3.5% Nacl Solution

Preparation and Electrochemical Properties of AlMgZnSnPbCuMnNi High Entropy Alloys with Low Free Corrosion Potentials

Performance of an Al–0.08Sn–0.08Ga–xMg Alloy As an Anode for Al–air Batteries in Alkaline Electrolytes

Exploring the Effect of Magnesium Content on the Electrochemical Performance of Aluminum Anodes in Alkaline Batteries

Effects of Indium, Gallium, or Bismuth Additions on the Discharge Behavior of Al-Mg-Sn-based Alloy for Al-air Battery Anodes in NaOH Electrolytes

The Electrochemical Behavior of Mg-Al-Zn-In-Ga Alloy As Anode Materials in Sodium Chloride Solution

Electrochemical Performance of Al-Mg Based Sacrificial Anodes

Electrochemical and microstructural investigations on an as-cast and solution-annealed Al–Mg–Sn–Ga alloy as anode material in sodium chloride solution

Corrosion Behavior Improvements of High Active Aluminum Alloy Anode in Alkaline Solution by Adding Inhibitors