Research on Preparation of ZnO Nanorods by Hydrothermal Steam Method

Kui-wei GENG,Li YANG,Qiang YIN,Ya-ru WANG,Long LUO

DOI: https://doi.org/10.16553/j.cnki.issn1000-985x.2015.10.045

2015-01-01

Abstract:Zn O nanorods were prepared by hydrothermal steam method. The products were characterized by XRD,SEM,PL spectra and Roman spectra. The results show that Zn O nanorods are highly- ordered arranged with the morphology of hexagonal prism structure. Along the c axis crystal preferential growth orientation,the vast majority of Zn O nanorods are perpendicular to the substrate. PL spectrum shows that intrinsic emission peak of Zn O nanorod is 385 nm. There are defect emission peaks among 433 nm,481 nm and 520 nm,which is probably caused by oxygen vacancy and Zn vacancy. When the growth temperature is 150 ℃,the strength of the emission peak between 450-550 nm is larger than at other temperatures. It probably because the higher temperature is,the faster growth speed and the more defects will be. Analysis of Raman scatter spectrum shows that the obvious characteristic peak of Zn O nanorod is at 437. 61 cm- 1,which is higher and has better crystallinity. There is a compressive stress due to the minimal mismatch of lattice. When the growth temperature is 120 ℃ and the growth time comes to 12 h,the created Zn O nanorods can reach 24 μm of length and 180 nm of width and 130∶ 1 of aspect ratio.