Abstract:In this study, K 2 TiF 6 and C powder (Ti:C atomic ratio 1:1) are introduced into Al-Si-Fe alloy by contact reaction method. The focus of this study is to investigate the reaction and precipitation behavior of Ti source in the alloy melt, and the effect of reaction products on the microstructure and properties of Al-Si-Fe alloy. The results show that the reaction products formed between Ti and the matrix alloy can destroy the acicular β-Fe phase in the original alloy. The transformation results in the a morphological change of the alloy from needle-like structure to Chinese script and fishbone-like structure, which effectively improves the mechanical properties of the alloy. The DSC analysis results indicate that Al-Si- Fe powder, K 2 TiF 6 powder, and C powder undergo significant exothermic reactions at around 950 °C, corresponding to the formation of TiC. Further microscopic morphology observations support the inference that TiC powders formed in this temperature range. Firstly, the synthesis of the matrix takes place at 580 °C. K 2 TiF 6 mixed with alloy powder shows an obvious exothermic peak at 660 °C, corresponding to the formation of the second phase Al 3 Ti by wetting and chemical reaction. However, it is worth noting that the reaction intermediate product(Al 4 C 3 phase) consumes three times as much Al 3 Ti as itself. As a result, the exothermic peak generated by Al 3 Ti disappears. Lastly, a long-term exothermic reaction that takes place above 850 °C lead to the gradual replacement of the Al 3 Ti phase by TiC particles. The mechanical properties test indicates that the needle-shaped Al 3 Ti to some extent deteriorates the alloy's properties. But the final product (TiC) can offset the deteriorating effect of Al 3 Ti and restore the alloy's property.

Prediction of the Thermodynamic Stability of TiC in Ni-Al Based Alloys

Computation and Analysis of Thermodynamics of Self-propagating High-temperature Synthesis TiC-Ni Cermets

Thermodynamic analysis of thermite reactions for synthesizing Ni-based alloys

In-situ TiC/Ti composites based on Ti 2 AlC–Ti system: Reaction process, microstructure, and mechanical properties

Thermodynamics of the Effect of Alloying Additions on In-Situ Reaction to Synthesize TiC/Mg Composites

First-Principle Study on the Stability of Lightly Doped (nb1–xtix)c Complex Carbides and Their Verification in 1045 Steel

Formation mechanism of Ti3AlC2 in TiO2–Al–C/TiC systems at high temperatures

Combustion Synthesis and Thermal Stability of Ti3AlC2

Microstructure Evolution of Ti-Al-C System Composite

Reaction mechanism and microstructure evolution of superhigh strength in-situ TiC/Ti composite based on Cr 2 AlC-Ti system

Fabrication and wear behavior of TiC/TiB 2 -reinforced NiAl intermetallic matrix composites

Formation of TiC/Ti 2 AlC and Α 2 +γ in In-Situ TiAl Composites with Different Solidification Paths

Ternary diffusion coefficients—Theoretical treatment and application to the In-situ -reinforced TiB 2 /Al composite

Thermodynamic Investigation on K2TiF6 and C Powder to Prepared in-situ TiCp in Molten Al-Si-Fe Alloy

TiC phase in Ti alloys at different temperatures

Effect of Reaction Heat on Reactive Joining of TiAl Intermetallics Using Ti–Al–C Interlayers

Reaction-induced nano-sized TiC in additive manufactured Ni-Co based superalloy

In-situ Production and Microstructure of TiC/Fe_3Al Composites

Role of Graphite on Microstructural Evolution and Mechanical Properties of Ternary TiAl Alloy Prepared by Arc Melting Method

Analysis of thermal stress in the TiC/Ti3AlC/Ti3Al three-phase composites

Ternary diffusion coefficients—Theoretical treatment and application to the <i>In-situ</i> -reinforced TiB<sub>2</sub>/Al composite