Abstract:Ni-doped TiO2 photocatalysts were prepared by low temperature combustion synthesis and some properties, such as optical absorption, crystal type, grain size distribution and chemistry transformation during temperature rising were characterized by UV-Vis DRS, X-ray diffraction (XRD), laser light dispersion grain size measurement machine and TG-DSC respectively. The photocatalytic activities of the prepared photocatalysts under visible light irradiation were evaluated by monitoring the degradation of methylene blue dye, a probe pollutant. The results indicate that the Ni-doped TiO2 photocatalysts prepared by low temperature combustion synthesis shift the optical absorption threshold to visible light, the band gap of 0.4 Ni-TiO2 (atomic ratio) is 2.3 eV, which corresponds to a 564 nm threshold in the visible light range. The crystal type of photocatalyst is anatase TiO2 and the content of NiTiO3 rise with the increase of Ni dopant. The grain size of photocatalyst distributes from 50 to 150nm, which account for 96.9% of entire quantity. During temperature rising, the TiO2 phase in photocatalyst transforms from amorphous structure to anatase and NiTiO3 crystallites appear at 445.2 degrees C. After 150 min visible light irradiation, 93.9% of methylene blue dye are degraded over 0.4 Ni-TiO2 photocatalyst. The photocatalytic activity of Ni doped TiO2 is higher than that of P25 under identical conditions.

Preparation of Photocatalytic Activity Nanosized TiO2 by Hydrolysis-Sol Method

Preparation and Photocatalytic Activities of TiO2 Nanotubes with Mixed Crystal Structure

The Thermal Analysis, Crystal Growth And Structure Transformation Of Nano-Scale Tio2 Prepared By Ticl4 Hydrolysis

Influence of Preparation Method on Morphology and Photocatalysis Activity of Nanostructured TiO2.

Influence Of Crystallization Of Nano Tio2 Prepared By Adsorption Phase Synthesis On Photodegradation Of Gaseous Toluene

Controllable Hydrothermal Synthesis, Optical and Photocatalytic Properties of TiO2 Nanostructures

Preparation and Properties of TiO2/Bentonite Composite Photocatalytic Materials at Room Temperature

Preparation of TiO_2 Nanoparticle and Their Photocatalytic Property

Preparation of Anatase-Type TiO_2 Nanoparticals from Ti (SO4)2 Solution under Hydrothermal Conditions and Its Photocatalytic Performance

Preparation of Nanoparticle WO_3-doped TiO_2 and Research on Its Photocatalytic Activity

Room‐Temperature Hydrolysis of Potassium Titanyl Oxalate and Water‐Assisted Crystallization for TiO2 with High Photocatalytic Activity

Effect of Calcination Temperature on Crystal Structure and Photocatalytic Prop- Erty of TiO2/Diatomite Nanoparticles

Preparation and Photocatalytic Activity of TiO<sub>2</sub>/Fe<sub>2</sub>O<sub>3 &Lt;/sub>nanocomposite

Low-Temperature Synthesis of Nanostructured TiO2 Particles and Their Photocatalytic Oxidation Activity

Preparation and Characterization of Nano-Tio2 Photocatalysts by Electrolysis Chemistry Method

PREPARATION OF IRON-DOPED TITANIA NANOCRYSTALLINE GRAINS AND ITS PHOTOCATALYTIC PROPERTY

Characterization and photocatalytic activity of Ni-doped tiO2 nano photocatalysts prepared by low temperature combustion synthesis]

Direct Continuous Hydrothermal Synthesis of High Surface Area Nanosized Titania

Effects of Water Amount and Ph on the Crystal Behavior of a TiO2 Nanocrystalline Derived from a Sol–Gel Process at a Low Temperature

Preparation of TiO2 Nanofibres and Influence of Calcination Temperature on Photocatalytic Activity

Hydrothermal Preparation and Photocatalytic Properties of Quantum Size TiO2 Nanoparticles