Multi-scale numerical simulation of the thermodynamic characteristics of Nb particles reinforced Zr-based amorphous composites by SLM
Yaqiong Ge,Jianfu Qiao,Zexin Chang,Min Hou,Haijun Xu,Anan Yang,Yue Song,Wenhao Bi,Ninshu Ma
DOI: https://doi.org/10.1016/j.mtcomm.2024.108597
IF: 3.8
2024-03-13
Materials Today Communications
Abstract:Room temperature brittleness is a critical factor that restricts the use of amorphous alloys. The approach taken involves the creation of amorphous composite materials by incorporating a second phase, aiming to overcome this critical challenge. This study established a comprehensive three-dimensional transient finite volume model to explore the process of producing niobium particles reinforced zirconium based amorphous alloys using laser selective melting technology. The model comprehensively considered physical transformations, including melting, wetting, spreading, and solidification of powder materials under laser irradiation, along with gravitational effects, surface tension, and evaporation recoil pressure. The investigation delved into the thermal effects and thermodynamic behavior of molten pool across composite material at multi-scales. The results showed that, when using a laser power of 90 W and a scanning speed of 1 m/s, Nb particles were partially melted or remain unmelted. These particles may exist in the molten pool's pores, enhancing the plasticity of amorphous materials. As laser power and scanning speed increased, defects such as sputtering and spheroidization emerge in the composite molten pool. The control of forming parameters could mitigate these defects. Importantly, the simulation results aligned well with experimental outcomes, bolstering the reliability and applicability of the finding. At the same time, the addition of Nb particles improved the plasticity of amorphous alloys.
materials science, multidisciplinary