Effect of ball-milling of glassy carbon powder on catalytic activities for tri-iodide reduction

Shun-jian XU,Yu-feng LUO,Wei ZHONG,Zong-hu XIAO,Yong-ping LUO

DOI: https://doi.org/10.3969/j.issn.1002-087X.2015.09.005

2015-01-01

Abstract:The refined glassy carbon particles with different size were obtained through changing the ball-milling time,and then employed as catalytic material for counter electrodes in dye-sensitized solar cells(DSC). The influence of ball-milling refinement on the catalytic activity of glassy carbons for reduction of tri-iodide in electrolyte was researched. The results show that the ball-milling refinement not only reduces the median particle size of glassy carbon from initial 20 μm to 6 μm after milling for 8 h, but also results in slight change of the crystal structure of glassy carbon. The layer distance d(002)of graphene sheets in glassy carbon gradually decreases from 0.364 nm to 0.353 nm.The variations of particle size and crystal structure affect catalytic active site on the surface of glassy carbon in different ways, resulting in the change of catalytic activity of glassy carbon. As ball-milling time increases, the catalytic activity increases firstly and then decreases,showing an optimum value at 2 h. The variation law of the photovoltaic properties of the glassy carbon based DSC with different ball-milling time follows the catalytic activity of glassy carbon.