In Situ Growth Large Area Silver Nanostructure on Metal Phenolic Network Coated NAAO Film and Its SERS Sensing Application for Monofluoroacetic Acid
Jiefang Sun,Dingshuai Xue,Wenchong Shan,Rui Liu,Runqing Liu,Huachao Zhao,Ting Li,Zhanhui Wang,Jing Zhang,Bing Shao
DOI: https://doi.org/10.1021/acssensors.1c00560
IF: 8.9
2021-06-03
ACS Sensors
Abstract:Rapid screening monofluoroacetic acid (FAcOH) is responsible for preventing chemical poisoning and food safety events. Whereas surface enhanced Raman scattering (SERS) spectra is an effective tool for detecting forbidden chemicals, it is difficult to directly detect FAcOH due to its small Raman scattering cross section as well as weak adsorption on SERS substrates. In this work, the metal phenolic supramolecular networks (MPNs, i.e., the tannic acid and Fe<sup>3+</sup> complex) were fabricated on the commercial nanoanodic aluminum oxide film (NAAO) for assisting in situ chemical deposition highly uniform Ag nanostructure over large areas (the ). The low cost and simple fabrication process made the a single-use consumable. For FAcOH detection, a specific derivative reaction between FAcOH and thiosalicylic acid (TSA) was introduced. By taking TSA as the Raman probe, its SERS signal attenuated constantly with the increasing amount of FAcOH. For improving quantitative accuracy, thiocyanate (SCN<sup>–</sup>) was introduced on the as an internal standard; thus, the characteristic peak intensity ratios associated with TSA and SCN<sup>–</sup> (<i>I</i><sub>1035</sub>/<i>I</i><sub>2125</sub>) were fitted to the concentration of FAcOH. It was demonstrated that the SERS assay achieved good sensitivity and selection toward FAcOH with the limit of quantitation (LOD) as low as 50 nmol L<sup>–1</sup>. The featured with highly sensitive, uniform, and consistent SERS performances could easily extend to wide SERS applications.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acssensors.1c00560?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acssensors.1c00560</a>.Sample preparation process, preparation of the TSA-AuNPs, and adsorption equilibrium results of TSA on the ; thioindigo chromogenic reaction; raw Raman mapping data; SERS enhancement of the interbatch samples; examination of the "coffee-ring" effect on the ; SEM images of Ag deposition on the aluminum foil and the NAAO as well as the ; SEM image of the AuNSs on the NAAO of different hole sizes; EDS analysis report for the /Fe<sup>3+</sup> (<a class="ext-link" href="/doi/suppl/10.1021/acssensors.1c00560/suppl_file/se1c00560_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
chemistry, multidisciplinary, analytical,nanoscience & nanotechnology