Abstract:Ce doped yttrium aluminum garnet(YAG∶Ce) spherical nanopowder was synthesized by dropping Al(NO3)3·9H2O,Y(NO3)3·6H2O and Ce(NO3)3·6H2O solution and ammonium hydrogen carbonate solution into the impinging streams reactor simultaneously at the same rate.The precursors and the YAG∶Ce powders were characterized by XRD,FT-IR,SEM and fluorescence spectrophotometer.The factors affecting the powder characteristics,including the mother salt concentration,the dropping speeds of solutions solution,and sintering methods and temperature were analyzed and discussed.The results show that the dispersion,the composition,the morphology and luminescence intensity of the YAG phosphors are affected remarkably by these factors.The YAG powders without any interphases can be obtained at 900℃ when the mother salt concentration(c0=0.055mol/L) is relatively low;the YAG phosphors including YAM,YAP and CeO2 impurity phases were prepared at 1000℃ when the mother salt concentration(c01.0mol/L) is high.The crystallinity can be increased with the increasing feeding rate at corresponding scope.The pure YAG phase could be obtained by Na2CO3-S-K2CO3 mixture flux calcination method at 700℃.Compared with the direct calcination method,the YAG∶Ce3+ phase transition temperature with the present method can be decreased about 300℃,and the luminescent intensity of as-prepared phosphor can be increased greatly than that prepared by direct baking method.

Highly Sinterable YAG Powder Derived from Thermal Decomposition of Carbonate Precursor

Co-Precipitation of YAG Powders for Transparent Materials: Effect of the Synthesis Parameters on Processing and Microstructure

Synthesis of Submicron-Sized Spherical Y2O3 Powder for Transparent YAG Ceramics

Ultrasonic Spray Co-Precipitation for YAG Nano-Powders Preparation

Preparation of Transparent YAG Ceramics via a Modified Solid-State Reaction Method

Preparation and Characterization of Monodispersed and Spherical YAG Powder for Transparent Ceramic by Spray Drying

Synthesis of Nd3+ Doped Nano-Crystalline Yttrium Aluminum Garnet (YAG) Powders Leading to Transparent Ceramic

Investigation on Factors Influencing the Synthesis of YAG Nano-powders by Co-precipitation Method

Formation Mechanism of Impure Phases and Crystallinity Investigation of YAG Powders Synthesized Via the Co-precipitation Method

Yag : Ce3+ Nanopowders: Synthesis, Characteristics And Luminescent Properties

Study on Preparation of Yttrium Oxide with Large Particle Sizes and Spherical Shapes by Precipitation with Ammonium Bicarbonate

Preparation of YAG Nano-Powders Via an Ultrasonic Spray Co-Precipitation Method

Preparation of YAG Nanoparticles by Sol-Gel and Their Application in Electrical Contact Material

Synthesis of Y2O3 nanopowders and transparent Y2O3 ceramics by carbonate-precipitation process

Preparation and Characterization of Y3Al5O12:Nd Phosphor Powders by Ultrasonic Atomization and Co-precipitation Process

Effect of Sintering Temperature on Properties of YAG Porous Ceramics via Atmospheric Sintering Method

The Preparation SiC/YAG Composite Powders by Co-Precipitation Method

Synthesis of YAG:Ce phosphor by impinging streams co-precipitation method

Rapid synthesis of Y3Al5O12 powders via plasma electrolysis

Fabrication and deagglomeration of YAG nanopowders

INFLUENCE OF PRECIPITANTS ON STRUCTURE OF COLLOIDAL SOLUTION SPRAY PYROLYSIS DERIVED Sm_(0.2)Ce_(0.8)O_(1.9) SOLID ELECTROLYTE