APPLICATION OF VN ALLOY IN PRODUCTION OF HRB400 REINFORCED BAR

冯运莉,齐长发

DOI: https://doi.org/10.3969/j.issn.1004-7638.2002.04.007

2002-01-01

Abstract:The application of VN alloy in the production of HRB400 reinforced bar was introduced. The properties and cost of 400MPa grade bar alloyed with FeV50 and VN were compared. The influence of VN alloy on the properties and microstructure was also studied. 

What problem does this paper attempt to address?

Research and development practice of HRB400 hot rolled ribbed steel bar

Run-sheng LIU,Yin-ping FAN

DOI: https://doi.org/10.3969/j.issn.1003-4226.2012.02.016

2012-01-01

Abstract:To introduce the process flow and characteristics of HRB400 hot rolled ribbed steel bar.The microalloying process,fine grain size technology and rolled rapidly cooling technology were adopted to make research and development practice of HRB400 hot rolled ribbed steel bar.Results show that the toughening effect of niobium in steel is the largest,in continuous casting the titanium steel produce a hole easily,which affects production,the production cost of vanadium alloying is higher than niobium alloying about 50 yuan per ton,in the condition of keeping strength almost the same,to adopt VN microalloying can save about 30% vanadium compare with VFe alloy.HRB400 hot rolled ribbed steel bar of quantity production diameter 12~32 mm series is decided to adopt VN microalloying process,the vanadium mass fraction added was 0.025%~0.035%.The ferrite grain size of fine grain size diameter 8 mm HRB400 ribbed steel bar is about 5~7 μm.The HRB400 high strength ribbed steel bar grain size researched by adopting rolled rapidly cooling technology increased 1~3 grade,yield strength is increased 50~100 MPa,production cost decreased about 50 yuan per ton,the surface secondary oxidized scale of finished steel decreased obviously,which improve product surface quality.
Iinfluence of alloying elements and hydrogen and oxygen on tensile properties of vanadium alloys

谌继明

DOI: https://doi.org/10.3969/j.issn.1005-0299.2002.04.007

2002-01-01

Abstract:Vanadium alloys are considered as one of the most promising candidate structural materials for a fusion reactor. Several V-Cr-Ti-Al-Si alloys developed in China were used in the test to study the influence of hydrogen, oxygen and alloying elements on their tensile properties for the purpose of finding ways to solve the hydrogen embrittlement of the alloy in fusion applications. Tensile tests were conducted for the alloys with different hydrogen concentrations. The results showed that Al, Si and Cr had strong solution hardening effect on the alloy. Al played a role to decrease the oxygen concentration level and thus the alloy with aluminum could have higher ductility. Hydrogen largely decreased the ductility of the alloy, and Al and Si elements caused the alloy more sensitive to the hydrogen embrittlement.
Strengthening mechanism of HRB400 rebar bearing chromium or vanadium

Huo Xiangdon

Abstract:The strengthening mechanism of HRB400rebar chromium and vanadium bearing is researched. The experimental results show that vanadium carbides and nitrides(VCN)precipitation have obvious effect on hardening.Austenite grain refinement can be achieved by deformation which induced VCN precipitation and inhibited austenite recrystallization.Combination of chromium and carbon in 20MnSiVCr steel decreases the diffusion of carbon,at the same time,chromium addition pushes the eutectoid transformation temperature to left in a phase diagram of iron-carbon.That is the main reason for volume fraction of pearlite increasing obviously.The strength of 20MnSiVCr is enhanced by precipitation hardening of VCN particles and pearlite strengthening.

Engineering,Materials Science
APPLICATION OF VN ALLOY IN PRODUCTION OF LARGE SIZE ANGLE STEEL

冯运莉,刘战英,陈春生,王云阁

DOI: https://doi.org/10.3969/j.issn.1004-7638.2004.02.008

2004-01-01

Abstract:Large size angle steel is mainly used in fabricating transmission tower. Tang Gang used 16Mn to produce Q345 grade angle steel. Owing to the narrow composition range, the production of Q345 grade angle steel is difficult. A new steel 16MnV(N) was designed by using V-Fe and VN alloy, which has better mechanical properties. The analysis in properties of 16Mn, 16MnV, 16MnV(N)angle steels shows that VN is a suitable alloy as microalloying large size and high strength angle steel.
MA-SPS-HIP Technique for Vanadium Alloys Preparation

Wu Cong,Li Chenhui,Zheng Pengfei,Fu Haiying,Chen Jiming

2014-01-01

Rare Metal Materials and Engineering

Abstract:This paper discussed the technical process of mechanical alloying-spark plasma sintering-hot isostatic pressing (MA-SPS-HIP) to fabricate vanadium alloy V-4Cr-4Ti-1.8YH(2), and the properties of the alloy after annealing treatment at 1000 similar to 4200 degrees C were tested. The XRD and SEM analyses show that it can reach the purpose of mechanical alloying after 50 h milling. The tensile test shows that V-4Cr-4Ti-1.8YH(2) alloy has a better mechanical property which can reach the optimum when the annealing temperature is 1100 degrees C. Microstructure analysis shows that the grain size of the vanadium alloy is mostly below 0.5 mu m, and YH2 transforms into Y2O3 during sintering process which are less than 50 nm particles distributing in the matrix.
Research on Low-Cost Vanadium Alloying in Producing Vanadium-Containing Seismic Resistant Rebar

Peng Tian,Zhiyong Zhong,Ruiguo Bai,Xingli Zhang,Chunliang Han,Hai Gao

DOI: https://doi.org/10.4028/www.scientific.net/amm.357-360.893

2013-01-01

Applied Mechanics and Materials

Abstract:The interception products of vanadium processing as vanadium alloys were studied in producing vanadium-containing seismic resistant rebar. The experimental results show that vanadium alloying with intermediate products was feasible and low-cost. Compared with conventional production process or ferrovanadium alloying, applied vanadium slag alloying in producing HRB335E could save 12.45 RMB per ton of steel, applied vanadium ball alloying in producing HRB400E could save 21.23 RMB per ton of steel, applied V-iron alloying in producing HRB400E could save 11.06 RMB per ton of steel.
Effects of Different Microalloying and Controlled Cooling Technology on Microstructure and Properties of 500mpa High-Strength Rebars

Wei Chen,Jian Chun Cao,Zhe Shi,Yin Hui Yang,Yu Zhao

DOI: https://doi.org/10.4028/www.scientific.net/amm.633-634.168

2014-01-01

Applied Mechanics and Materials

Abstract:The mechanical properties and microstructures of three different VN, Nb, V-Nb microalloyed rebars were investigated by using tensile testing machine, impact machine, metallographic microscopy, scaning electron microcopy, transmission electron microscopy and X-ray diffraction apparatus. The results showed that the microstructure of V-Nb microalloyed specimen is consisted of ferrite, pearlite and a small amount of fine bainite (6.7wt%), and obvious effect of grain refinement was obtained with more than 10 size grade of ferrite grain, showing optimal comprehensive properties. SEM micrograph of tensile fracture surface for V-Nb microalloyed 500MPa high-strength rebar is dimple and ductile, ductile-brittle transformation temperature is lower than-30°C, which has good plasticity-toughness and impact toughness at low temperature. The results of precipitates have shown that a large number of small and dispersive V(CN) and Nb (CN) precipitates with size of 5~30nm are formed, good effect of precipitation strengthening was achieved in 500MPa high-strength rebars produced by different microalloying and controlled cooling technology.
Strengthening Mechanisms and Microstructure of Vanadium and Nitrogen Microalloyed High Strength Seismic Rebar

Jianchun Cao,Dongwei Zhao,Wei Chen,Zhe Shi,Weidong Zhao

DOI: https://doi.org/10.4028/www.scientific.net/amr.450-451.600

2012-01-01

Advanced Materials Research

Abstract:Using metallographic test, physicochemical phase analysis, X-ray diffraction and transmission electron microscope, the microstructure of seismic rebars with yield strength of 500MPa, which were fabricated by vanadium and nitrogen microalloying and controlled rolling and controlled cooling, were investigated. The results of metallographic test show that the microstructure in centre and interlayer of tested rebar samples are made up of ferrite, pearlite and a small amount of bainite, but tempered sorbite with thickness of 0.9mm on the edge of the rebars. Physicochemical phase analysis indicates that vanadium in the rebars had precipitated by VN mainly, and the precipitation rates of V and N are 60% and 70%, respectively. The result of strengthening mechanisms analysis shows that fine grain strengthening and transformation strengthening are the dominated contributions to strength and strengthening increments of them are 184.4 MPa and 111.6 MPa, respectively.
BRITTLENESS OF VANADIUM ALLOYS USED IN FUSION ENVIRONMENTS

谌继明

DOI: https://doi.org/10.3969/j.issn.1002-6495.2002.06.002

2002-01-01

Abstract:The brittleness of several V-Cr-Ti-Al-Si alloys caused by the pickup of oxygen and hydrogen in fusion reactor environments was studied by using a simulation method of high temperature oxidation and hydrogenation.The neutron irradiation induced ductility loss was also studied by using experimental data from references.The results showed that the oxidation kinetic of V4Cr4Ti alloy exhibited parabolic behavior in a flowing argon gas with low partial pressure oxygen from 450℃ to 600℃.Alloys showed a ductility loss with increasing oxygen concentration with an exception of V4Ti3Al alloy.The alloys showed much stronger sensitivity to hydrogen embrittlement when hydrogen acts synergistically with oxygen.Neutron irradiation,especially those at temperature lower than 400℃,caused great loss in the ductility of the alloys or even brittle failure under tensile test.It was also found that hydrogen,neutron irradiation and strain hardening had the same tendency to reduce the ductility of the alloys.So it was supposed that a way of fine grain strengthening should be taken to improve the properties of the alloys against the hydrogen embrittlement and the neutron irradiation induced brittleness.
Hot Ductility Behaviors of HRB600 Vanadium-Containing Steel Rebar

Peng Tian,Zhi Yong Zhong,Rui Guo Bai,Xing Li Zhang

DOI: https://doi.org/10.4028/www.scientific.net/amr.898.68

2014-01-01

Advanced Materials Research

Abstract:Hot ductility behaviors of HRB600 vanadium-containing steel rebar was study with thermal simulation test and the fracture was observed and analyzed by scanning electron microscope (SEM). The result shows that, the contraction ratio of cross sectional area (Z) in 1050°C - 1300°C was more than 60%, tensile sample showed good ductility; Z in 750°C-1000°C was less than 60%, tensile sample showed brittle, namely third brittle zone. Then third brittle zone should be avoided or minimize stays in the development process of continuous casting and hot rolling. The fracture mode and the morphology of fracture surfaces were different at different temperatures.
500Mpa Seismic Rebars Developed by Nitrogen-Rich and Vanadium-Microalloyed, Controlled Cooling Technology

Wei Chen,Zhe Shi,Yu Zhao,Jianchun Cao,Yumei Yu

DOI: https://doi.org/10.4028/www.scientific.net/amr.189-193.752

2011-01-01

Advanced Materials Research

Abstract:500MPa high-strength seismic rebars was developed by nitrogen-rich & vanadium -microalloyed, controlled cooling technology in domestic steel plant of china, microalloy precipitates, microstructure, mechanical properties, welding performance and aging properties of rebars were researched by using metallographic microscopy, scaning electron microcopy, transmission electron microscopy, x-ray diffraction apparatus, flash-butt welding and mechanical properties testing. The results show that a large number of the dispersed V (C, N) precipitates are precipitated in the grain boundary, dislocation line and the ferrite matrix, precipitation size in the ferrite matrix is 10~ 20nm, V(C,N) precipitates amount accounts for 67.54% of the total amount of vanadium in steel, effect of precipitation strengthening is remarkable; when termination temperature after controlled cooling for rebars is controlled at 710°C ～750°C , the core microstructure is polygonal ferrite and pearlite, ferrite grain grade is 11.0, outer layer microstructure is acicular ferrite, pearlite and a small amount of bainite, good effects on fine-grain strengthening and seismic performance are obtained; rebars have low strain aging and good welding performance; production cost is reduced by RMB 100 Yuan per ton steel compared with VN micro-alloyed and hot-rolling process, benefit is obvious.
Effect of Nb-V different micro-alloying on tensile fracture behavior of high strength rebar

邓蕾,曹建春,周晓龙,陈伟,李丹,杨银辉

DOI: https://doi.org/10.13289/j.issn.1009-6264.2013.s1.015

2013-01-01

Abstract:Effect of Nb-V different micro-alloying on tensile fracture behavior of high strength rebar was characterized by tensile test, optical optical microscope, SEM combined with energy energy spectrum analysis and TEM. The results indicate that the microstructure in center of tested rebar consists of consists of ferrite, pearlite and bainite. The bainite volume fraction (50%-3%) decreases with the decreasing Nb content. The tensile fracture exhibits typical ductile fracture with dimples. The size and depth of dimples begin to increase and then decrease with the decreasing bainitevolume fraction. The inclusions of crack and fracture are mainly of MnS and oxides. Micro-cracks are mostly formed in interfaces or inclusions, also in ferrite matrix. Micro-cracks size increases with decreasing bainite volume fraction. Crack would expand into the ferrite while it comes across bainite during the extension.
Effects of controlled cooling temperature on microstructure and peformance of V-Nb microalloyed high-strength rebars

陈伟,施哲,陈红,曹建春,赵宇

DOI: https://doi.org/10.13289/j.issn.1009-6264.2013.10.012

2013-01-01

Abstract:In view of 500 MPa grade high-strength rebars V-Nb microalloyed by controlled cooling process in domestic steel plant, the effects of controlled cooling temperature after finishing rolling on microstructure, grain size, hardness and precipitates of the rebars were investigated by thermal simulation, SEM, hardness test, TEM and XRD. The results show that, when controlled cooling temperature is controlled in the range of 720-740°C, microstructure of the tested steel consists of ferrite, pearlite and a small amount of bainite (6%-15% mass factron), ratio and shape of phases in the microstructure is better, is favorable for improvement of strength, toughness and ductility of the rebars, the size grade of ferrite grain is in the range of 10.5-11.0, obvious effect of fine grain strengthening and anti-seismic performance are obtained; Vickers hardness of the tested steel is 208-213 HV, the corresponding tensile strength(Rm) increases from 700 MPa to 720 MPa. The size of a lot of small V (CN) and Nb (CN) precipitates is in the range of 5-30 nm, which distributes on grain boundary dislocation lines and within ferrite matrix, and the precipitate fraction is 70%. The excellent effect of precipitation strengthening and grain refinement are obtained for the steel by the controlled cooling process.
Investigation on the Strengthening and Toughening Mechanism of 500 Mpa V-Nb Microalloyed Anti-Seismic Rebars

Wei Chen,Jianchun Cao,Yinhui Yang,Zhe Shi,Weiqiang Zhang,Min Huang

DOI: https://doi.org/10.5755/j01.ms.21.4.9710

2015-01-01

Abstract:Two types of 500 MPa anti-seismic rebars were produced by V-Nb microalloyed combined with controlled rolling and cooling technology, the strengthening and toughening mechanism of which were investigated. The complex phase microstructures of specimens consist of ferrite, pearlite and bainite (6 – 10 %). Furthermore, a large number of V(C,N) and Nb(C,N) precipitates with size of 5 – 30 nm formed in the ferrite matrix, grain boundaries and on dislocation lines, promoting the precipitation strengthening and inhibiting grain coarsening to controlled cooling microstructure. The mechanical performance of the steels was improved by solution and grain refinement strengthening, precipitation and microstructure strengthening. And the best strengthening effect was obtained by grain refinement, which increased the yield strength more than 35 % strength increment contribution ratio to yield strength. Moreover, about 16.5 % microstructure strengthening increment was obtained due to bainite formation. The plasticity and low-temperature toughness enhancement were mainly attributed to ferrite grain refinement improvement.DOI: http://dx.doi.org/10.5755/j01.ms.21.4.9710
Application of Different Vanadium Alloys in Steel

P. Tian,Z. Y. Zhong,R. G. Bai,X. L. Zhang,H. Gao

DOI: https://doi.org/10.2991/cisia-15.2015.231

2015-01-01

Abstract:The current status of vanadium bearing steel and characteristics of different vanadium alloys were analyzed, the effect of different vanadium alloys on V absorption rate and steel properties was investigated, and the varieties of steel properties and V/N ratio under different nitrogen conditions were discussed. It could be concluded that the ferrovanadium should be used mainly in the steel with strict limits on nitrogen content and the ferrovanadium nitride would be preferred in vanadium-nitrogen strengthened steel. The vanadium-nitrogen strengthening can be enhanced with nitrogen-bearing vanadium alloy, which is in favor of cost reduction. The V/N ratio should be in the range of 4 to 6 in commercial production with the optimum ratio of 4.5.
Effect of Nitrogen Content and Cooling Rate on Transformation Characteristics and Mechanical Properties for 600 MPa High Strength Rebar

Jing Zhang,Fu-ming Wang,Chang-rong Li,Zhan-bing Yang

DOI: https://doi.org/10.1515/htmp-2015-0080

2016-10-01

High Temperature Materials and Processes

Abstract:Abstract To obtain appropriate chemical composition and thermo-mechanical schedules for processing the V-N microalloyed 600 MPa grade high strength rebar, the microstructure analysis during dynamic continuous cooling and tensile tests of three experimental steels with different nitrogen contents were conducted. The results show that increasing nitrogen content promotes ferrite transformation and broadens the bainite transformation interval, when the nitrogen content is in the range of 0.019–0.034 mass%. Meanwhile, the martensite start temperatures decrease and the minimal cooling rate to form martensite increases. To achieve a good combination of strength and ductility, the cooling rates should be controlled in the range of 0.5–3°C/s, leading to the microstructure of ferrite, pearlite and less than 10% bainite (volume fraction). Furthermore, all the experimental steels satisfy the performance requirement of 600 MPa grade rebar and the rebar with nitrogen content of 0.034 mass% shows the highest strength through systematically comparative investigation.

materials science, multidisciplinary
Fatigue Performance of Microalloyed High-strength Rebar and Analysis of Fracture Mechanism

Peng-yan Lu,Yu Liu,Hua-jie Wu,Gang Liu,Xiang Meng,Yang Xu

DOI: https://doi.org/10.1016/s1006-706x(15)30126-6

2015-01-01

Abstract:Fatigue performance of hot-rolled ribbed-steel bar with the yield strength of 500 MPa (HRB500) was studied with bend-rotating fatigue test at a stress ratio of R = − 1. It is determined by staircase method that its fatigue strength for 107 cycles is 451 MPa, which is higher than that of common carbon structural steel. This should be attributed to the fine-grain strengthening resulting from the high content of alloy element V and Thermo-Mechanical Control Process (TMCP). The S-N curve function is also obtained by nonlinear regression with three parameters power function. The fatigue fractures of the specimen were further analyzed with Scanning Electron Microscopy (SEM) and Energy Disperse Spectroscopy (EDS) to study the fracture mechanism. Taking into account microstructure, hardness and cleanliness of the material, it implies that the fatigue fractures of HRB500 rebar all arise from surface substrates in which many brittle inclusions are contained, and that the fatigue crack propagation is principally based on the mechanism of quasi-cleavage fracture, because of the intracrystalline hard spots leading to stress concentration and thus to the cracks. Moreover, the transient breaking area exhibits microvoid coalescence of ductile fracture due to the existing abundant inclusions.
Development of Air-Cooled Super Strength Finish Rolled Rebar

LI Wen-tao,LI Zheng-cao,ZHANG Han,BAI Bing-zhe

DOI: https://doi.org/10.13228/j.boyuan.issn0449-749x.2011.05.006

2011-01-01

Abstract:Super strength finish rolled rebar based on air-cooled was studied in laboratory and industrial production was carried out.Vanadium microalloyed was developed on the base of manganese series bainitic steels in order to improve performance,reduce costs and simplify technology.Besides,morphology,size and distribution of vanadium precipitates were studied by use of TEM.The air-cooled bainite steel developed without expensive alloy elements shows high strength and low yield ratio,which fully meets the standard of PSB 1080.20mm rebar has mechanical properties as follows: Rm 1600-1610MPa;ReL 1400-1420MPa;A 8.5%;Agt 5.0%.32mm rebar: Rm 1450-1500MPa;ReL 1140-1200MPa;A 9.0%;Agt 5.0%.
Effect of V on Strength and Toughness of Low Alloyed Air-Cooled MnSiCr Bainite/Martensite Multiphase Steels

LI Wen-tao,LI Zheng-cao,BAI Bing-zhe

2010-01-01

Abstract:Secure reactor structure plays the role of containing radioactive substances and protecting system from the interference of reactor,which is related to the safe operation of the power,so it is an important structure. Nuclear reactor cylinder prestressed concrete structure with pure rolling steel rebar directly influences the tenacity of secure life. Vanadium microalloyed super strength finish rolled rebar based on air-cooled Mn series bainitic steels was developed in order to meet the needs. Yield strength of vanadium-alloyed air-cooled tempering steel reaches 1 494 MPa,and tensile strength is 1 688 MPa. Effect of vanadium on the strength and snugness,structure and phase transformation was studied by means of SEM and TEM. Besides,morphology,size and distribution of vanadium precipitates were studied.
The Influence of Vanadium Element on the Microstructure and Mechanical Properties of (Feconi)100-Xvx High-Entropy Alloys

Zhenhua Ye,Chuanwei Li,Xinyu Zhang,Yu Liao,Jianfeng Gu

DOI: https://doi.org/10.1016/j.matchar.2022.112232

IF: 4.537

2022-01-01

Materials Characterization

Abstract:Despite their unique thermodynamic and kinetic features, Face-centered cubic (FCC) high-entropy alloys (HEAs) are well known to usually possess superior ductility at room temperature but relatively low strength, which greatly limits their structural application. To address this issue of strength-ductility tradeoff, we have systematically investigated in the present work the crystallographic structure, microstructural evolution, and tensile properties of (FeCoNi)100-xVx (x = 10, 15, 20, 25, and 30) HEAs in both as-quenched and annealed conditions. A single-phase solid solution was still obtained by quenching from high temperature when the V concentration was up to 25%. It is interesting to find in that the microstructure of this family of HEA alloys varies with the content of V element and pre-annealing, showing an unusual single phase with L12 chemically ordered structure for (FeCoNi)75V25, but otherwise a composite consisting of a L12 phase coherent with disordered FCC phase matrix for the other V doped FeCoNi alloys such as (FeCoNi)80V20. Owing to the presence of the ordered phase, both (FeCoNi)80V20 and (FeCoNi)75V25 display a remarkable work hardening capability, leading to the enhanced ultimate tensile strengths up to 1.1 and 1.4 GPa, respectively, and the resultant excellent deformability with uniform plastic strain of >30%.

APPLICATION OF VN ALLOY IN PRODUCTION OF HRB400 REINFORCED BAR

Research and development practice of HRB400 hot rolled ribbed steel bar

Iinfluence of alloying elements and hydrogen and oxygen on tensile properties of vanadium alloys

Strengthening mechanism of HRB400 rebar bearing chromium or vanadium

APPLICATION OF VN ALLOY IN PRODUCTION OF LARGE SIZE ANGLE STEEL

MA-SPS-HIP Technique for Vanadium Alloys Preparation

Research on Low-Cost Vanadium Alloying in Producing Vanadium-Containing Seismic Resistant Rebar

Effects of Different Microalloying and Controlled Cooling Technology on Microstructure and Properties of 500mpa High-Strength Rebars

Strengthening Mechanisms and Microstructure of Vanadium and Nitrogen Microalloyed High Strength Seismic Rebar

BRITTLENESS OF VANADIUM ALLOYS USED IN FUSION ENVIRONMENTS

Hot Ductility Behaviors of HRB600 Vanadium-Containing Steel Rebar

500Mpa Seismic Rebars Developed by Nitrogen-Rich and Vanadium-Microalloyed, Controlled Cooling Technology

Effect of Nb-V different micro-alloying on tensile fracture behavior of high strength rebar

Effects of controlled cooling temperature on microstructure and peformance of V-Nb microalloyed high-strength rebars

Investigation on the Strengthening and Toughening Mechanism of 500 Mpa V-Nb Microalloyed Anti-Seismic Rebars

Application of Different Vanadium Alloys in Steel

Effect of Nitrogen Content and Cooling Rate on Transformation Characteristics and Mechanical Properties for 600 MPa High Strength Rebar

Fatigue Performance of Microalloyed High-strength Rebar and Analysis of Fracture Mechanism

Development of Air-Cooled Super Strength Finish Rolled Rebar

Effect of V on Strength and Toughness of Low Alloyed Air-Cooled MnSiCr Bainite/Martensite Multiphase Steels

The Influence of Vanadium Element on the Microstructure and Mechanical Properties of (Feconi)100-Xvx High-Entropy Alloys