Abstract:A coordination-assisted synthetic approach is reported here for the synthesis of highly active and stable gold nanoparticle catalysts in ordered mesoporous carbon materials using triblock copolymer F127 as a structure-directing agent, thiol-containing silane as a coordination agent, HAuCl4 as a gold source, and phenolic resin as a carbon source. Upon carbonization, the gold precursor becomes reduced to form monodispersed Au nanoparticles of ca. 9.0 nm, which are entrapped or confined by the "rigid" mesoporous carbonaceous framework. Nanoparticle aggregation is inhibited even at a high temperature of 600 degrees C. After removal of the silica component, the materials possess the ordered mesostructure, high surface area (similar to 1800 m(2)/g), large pore volume (similar to 1.19 cm(3)/g), and uniform bimodal mesopore size (<2.0 and 4.0 nm). The monodispersed gold nanoparticles are highly exposed because of the interpenetrated bimodal pores in the carbon framework, which exhibit excellent catalytic performance. A completely selective conversion of benzyl alcohol in water to benzoic acid can be achieved at 90 degrees C and 1 MPa oxygen. Benzyl alcohol can also be quantitatively converted to benzoic acid at 60 degrees C even under an atmospheric pressure, showing great advantages in green chemistry. The catalysts are stable, poison resistant, and reusable with little activity loss due to metal leaching. The silane coupling agent played several functions in this approach: (1) coordinating with gold species by the thiol group to benefit formation of monodispersed Au nanopartides; (2) reacting with phenolic resins by silanol groups to form relatively "rigid" composite framework; (3) pore-forming agent to generate secondary pores in carbon pore walls, which lead to higher surface area, larger pore volumes, and higher accessibility to to the gold nanopartides. Complete removal of the silica component proves to have little effect on the catalytic performance of entrapped Au nanoparticles.

Dispersed gold nanoparticles supported in the pores of flower-like macrocellular siliceous foams based on an ionic liquid as catalysts for reduction

Synthesis and assembly of gold nanoparticle-doped polymer solid foam films at the liquid/liquid interface and their catalytic properties.

Facile And Controllable Fabrication Of Gold Nanoparticles-Immobilized Hollow Silica Particles And Their High Catalytic Activity

In Situ Growth of Gold Nanoparticles on SiO2/lanthanide–polyoxometalates Composite Spheres: an Efficient Catalytic and Luminescent System

Morphology and Composition Controlled Synthesis of Flower-Like Silver Nanostructures.

Synthesis and deposition of ultrafine noble metallic nanoparticles on amino-functionalized halloysite nanotubes and their catalytic application

Aggregation-Free Gold Nanoparticles In Ordered Mesoporous Carbons: Toward Highly Active And Stable Heterogeneous Catalysts

Macrocellular Polymer Foams from Water in Oil High Internal Phase Emulsion Stabilized Solely by Polymer Janus Nanoparticles: Preparation and Their Application As Support for Pd Catalyst

Gold Nanoparticle Stabilization Within Tailored Cubic Mesoporous Silica: Optimizing Alcohol Oxidation Activity

Controllable Preparation of Monodisperse Mesoporous Silica from Microspheres to Microcapsules and Catalytic Loading of Au Nanoparticles

Amine oxide surfactant-mediated synthesis of plate-based gold nanocrystals with tunable surface wrinkles and their applications in the ethylene glycol oxidation reaction

Facile Fabrication of Nanoporous Au–Pd Bimetallic Foams with High Catalytic Activity for 2-Nitrophenol Reduction and SERS Property

Morphology-selective synthesis of active and durable gold catalysts with high catalytic performance in the reduction of 4-nitrophenol

Facile Synthesis of Size Controllable Dendritic Mesoporous Silica Nanoparticles

Synthesis of Mesoporous Silica Hollow Nanospheres with Multiple Gold Cores and Catalytic Activity

Gold Nanoparticle Morphology Adjusted as High-performance Catalyses in Supergiant Dispersant

Synthesis of Stable Au–SiO2 Composite Nanospheres with Good Catalytic Activity and SERS Effect

Mesostructured cellular foam silica supported Au–Pt nanoalloy: Enrichment of d-state electrons for promoting the catalytic synergy

Hollow mesoporous organosilica nanospheres with multiple tiny silver nanoparticles: A polymer mediated growth approach and catalytic application

Hollow mesoporous aluminosilica spheres with perpendicular pore channels as catalytic nanoreactors

Controllable Synthesis of Water-Soluble Gold Nanoparticles and Their Applications in Electrocatalysis and Surface-Enhanced Raman Scattering.