Abstract:A coordination-assisted synthetic approach is reported here for the synthesis of highly active and stable gold nanoparticle catalysts in ordered mesoporous carbon materials using triblock copolymer F127 as a structure-directing agent, thiol-containing silane as a coordination agent, HAuCl4 as a gold source, and phenolic resin as a carbon source. Upon carbonization, the gold precursor becomes reduced to form monodispersed Au nanoparticles of ca. 9.0 nm, which are entrapped or confined by the "rigid" mesoporous carbonaceous framework. Nanoparticle aggregation is inhibited even at a high temperature of 600 degrees C. After removal of the silica component, the materials possess the ordered mesostructure, high surface area (similar to 1800 m(2)/g), large pore volume (similar to 1.19 cm(3)/g), and uniform bimodal mesopore size (<2.0 and 4.0 nm). The monodispersed gold nanoparticles are highly exposed because of the interpenetrated bimodal pores in the carbon framework, which exhibit excellent catalytic performance. A completely selective conversion of benzyl alcohol in water to benzoic acid can be achieved at 90 degrees C and 1 MPa oxygen. Benzyl alcohol can also be quantitatively converted to benzoic acid at 60 degrees C even under an atmospheric pressure, showing great advantages in green chemistry. The catalysts are stable, poison resistant, and reusable with little activity loss due to metal leaching. The silane coupling agent played several functions in this approach: (1) coordinating with gold species by the thiol group to benefit formation of monodispersed Au nanopartides; (2) reacting with phenolic resins by silanol groups to form relatively "rigid" composite framework; (3) pore-forming agent to generate secondary pores in carbon pore walls, which lead to higher surface area, larger pore volumes, and higher accessibility to to the gold nanopartides. Complete removal of the silica component proves to have little effect on the catalytic performance of entrapped Au nanoparticles.

Synthesis of Mesoporous Silica Hollow Nanospheres with Multiple Gold Cores and Catalytic Activity

One-pot synthesis of thermally stable gold@mesoporous silica core-shell nanospheres with catalytic activity

Synthesis of Stable Au–SiO2 Composite Nanospheres with Good Catalytic Activity and SERS Effect

Preparation of Core–shell Structured Au@SiO2 Nanocomposite Catalyst with Au Core Size below 2 Nm Without High-Temperature Calcination Procedure

Hollow mesoporous aluminosilica spheres with perpendicular pore channels as catalytic nanoreactors

Preparation of Highly Active Silica-Supported Au Catalysts for Co Oxidation by A Solution-Based Technique

Controllable Preparation of Monodisperse Mesoporous Silica from Microspheres to Microcapsules and Catalytic Loading of Au Nanoparticles

Synthesis of multiple Ag nanoparticles loaded hollow mesoporous carbon spheres for highly efficient and recyclable catalysis

Synthesis of Silica/carbon-Encapsulated Core-Shell Spheres: Templates for Other Unique Core-Shell Structures and Applications in in Situ Loading of Noble-Metal Nanoparticles.

Core–shell magnetic mesoporous 3-aminophenol–formaldehyde resin microspheres with rich functional groups via interface co-assembly and polymerization

Mesoporous SiO2 Yolk Shell Confined Core-Satellite Ag Nanoparticles: Preparation and Catalytic Activity

Hollow mesoporous organosilica nanospheres with multiple tiny silver nanoparticles: A polymer mediated growth approach and catalytic application

In Situ Growth of Gold Nanoparticles on SiO2/lanthanide–polyoxometalates Composite Spheres: an Efficient Catalytic and Luminescent System

Facile 'embedding' of Au Nanocrystals into Silica Spheres with Controllable Quantity for Improved Catalytic Reduction of P-Nitrophenol

A General and Feasible Method for the Fabrication of Functional Nanoparticles in Mesoporous Silica Hollow Composite Spheres

Controlled Synthesis of N-Doped Carbon Nanospheres with Tailored Mesopores through Self-Assembly of Colloidal Silica.

Preparation of SiO2@Au@TiO2 Core–shell Nanostructures and Their Photocatalytic Activities under Visible Light Irradiation

Facile And Controllable Fabrication Of Gold Nanoparticles-Immobilized Hollow Silica Particles And Their High Catalytic Activity

Novel Hollow Sub-Microspheres with Movable Au Nanoparticles and Excessive Pt Nanoparticles in Core and Silica As Shell

Aggregation-Free Gold Nanoparticles In Ordered Mesoporous Carbons: Toward Highly Active And Stable Heterogeneous Catalysts

A versatile ligand-assisted cooperative template method to synthesize multi-shelled mesoporous hollow metal hydroxide and oxide nanospheres as catalytic reactors