Abstract:Continuous silicon carbide fiber–reinforced silicon carbide matrix (SiCf/SiC) composites have developed into a promising candidate for structural materials for high–temperature applications in aerospace engine systems. This is due to their advantageous properties, such as low density, high hardness and strength, and excellent high temperature and oxidation resistance. In this study, SiCf/SiC composites were fabricated via polymer infiltration and pyrolysis (PIP) with the lower–oxygen–content KD–II SiC fiber as the reinforcement; a mixture of 2,4,6,8–tetravinyl–2,4,6,8–tetramethylcyclotetrasiloxane (V4) and liquid polycarbosilane (LPCS), known as LPVCS, was used as the precursor; while pyrolytic carbon (PyC) was used as the interface. The effects of oxidation treatment at different temperatures on morphology, structure, composition, and mechanical properties of the KD–II SiC fibers, SiC matrix from LPVCS precursor conversion, and SiCf/SiC composites were comprehensively investigated. The results revealed that the oxidation treatment greatly impacted the mechanical properties of the SiC fiber, thereby significantly influencing the mechanical properties of the SiCf/SiC composite. After oxidation at 1300°C for 1h, the strength retention rates of the fiber and composite were 41% and 49%, respectively. In terms of the phase structure, oxidation treatment had little effect on the SiC fiber, while greatly influencing the SiC matrix. A weak peak corresponding to silica (SiO2) appeared after high–temperature treatment of the fiber; however, oxidation treatment of the matrix led to the appearance of a very strong diffraction peak that corresponds to SiO2. The analysis of the morphology and composition indicated cracking of the fiber surface after oxidation treatment, which was increasingly obvious with the increase in the oxidation treatment temperature. The elemental composition of the fiber surface changed significantly, with drastically decreased carbon element content and sharply increased oxygen element content.

The Study on Oxidation Behavior of Short Carbon Fiber Reinforced Silicon Carbide Composites

Oxidation Kinetics and Its Impact on the Strength of Carbon Short Fiber Reinforced C/SiC Ceramics

Oxidation behaviors of carbon fiber reinforced multilayer SiC-Si3N4 matrix composites

Oxidation behavior of 3D SiCf/SiBCN composites at 800–1200 °C

Mechanical and Oxidation Properties of C/SiC Corrugated Lattice Core Composite Sandwich Panels

Oxidation Behavior of Short SiC Fibers-Reinforced Glass-Ceramic Composites

Effect of oxidation on internal friction behavior of C/SiC composites

Stress‐Oxidation Behavior of a Carbon/Silicon Carbide Composite in a High‐Temperature Combustion Environment

Oxidation Behavior of SiC/SiC Composites in Air at High Temperature

Insight into the origin of oxidation behaviors of carbon fiber reinforced carbon aerogel composites with different porous skeletons

Influence of Oxidation Damages on Mechanical Properties of SiC/SiC Composite Using Domestic Hi-Nicalon Type SiC Fibers

Long-term oxidation and ablation behavior of C<sub>f</sub>/ZrB<sub>2</sub>-SiC composites at 1500, 2000, and 2200C

Oxidation Behaviour of C–SiC–ZrC Composite

Oxidation Resistance Behavior of Short Carbon Fiber Reinforced ZrB2,-SiC Composites

Effect of Oxidation Time on Fracture Behavior of C/SiC Composites at 800 °C in Air

Study on the oxidation resistance of carbon ceramic composite

Effect of Oxidation Treatment on KD–II SiC Fiber–reinforced SiC Composites

Oxidation Resistance of Dense Carbon Fiber/si–o–c Glass Composite Fabricated by Pre-Oxidation and Spark Plasma Sintering

Long-time oxidation behavior of the nearly stoichiometric polycrystalline SiC fibers under air atmosphere at different temperatures

Non-Destruction Evaluation Method for Long-Term Oxidation Behavior of SiC/SiC Composites with Different Preforms in Wet Oxygen

Inoxidizable Behavior of SiC Reinforced MoSi_2 Composite Prepared by Infiltration Method