Abstract:The formation of a uniform Fe-Al inhibition layer with a proper thickness at steel interface during continuous hot-dip galvanizing process is a crucial issue for industrial production. The inhibition layer prohibits the nucleation and growth of brittle Fe-Zn intermetallic compounds which deteriorate the adhesion of the galvanizing coating and result in an inhomogeneous distribution of the coating. The inhibition layer was identified to be Fe2Al5 with some Zn dissolved in it. But Fe2Al5 inhibition layer was damaged with galvanized time increasing, will lose the inhibition to the Fe- Zn reaction. Nevertheless, there is no systematic and comprehensive investigation the causes of the inhibition layer is damaged. The aim of this work is to clarify the destabilization mechanism of Fe2Al5 inhibition layer. In the present study, the mass fraction of 0.2%Al was added into the zinc bath at 450 degrees C for hot dip galvanizing. SEM was used to observe the structure characteristics of the hot-dip galvanized coating. EDS was used to quantitatively analyze the micro area components of phases and also Used its line scan and mapping scan to qualitatively analyze the element change of the coating cross section. By means of the Miedema model and the Toop model, the thermodynamic values of the binary Fe-Al, Fe-Zn and ternary Fe2Al5Znx (eta) intermetallic compounds (IMC) in the coatings were calculated. The fundamental reason for the Fe-Zn reaction caused by Fe2Al5 destabilization with galvanized time increasing was analyzed. The results show that because Fe-Al IMC which is generate preferentially had more stable thermodynamic property than Fe-Zn IMC, the continuous Fe2Al5 intermetallic compound inhibition layer was produced preferentially at steel and zinc bath interface which inhibit the Fe-Zn reaction. However, with the galvanized time increasing, Fe2Al5 destabilization which led to the loss of inhibitory effect of Fe-Zn reaction and produced FeZn10 (delta). There are two kinds of destabilization mechanism of Fe2Al5 inhibition layer, one is that the local depletion of Al at Fe2Al5 and zinc bath interface result in erosion of Fe2Al5 by Zn and the formed Fe2Al5Znx caused the decrease of the systematic thermodynamic stability which led to erosion and decomposition of Fe2Al5 by Zn. At the same time, FeZn10 (delta) phase was produced between the Fe2Al5 and zinc bath interface. The phase transformation process can be described as: Fe2Al5 ->eta -> L+eta+delta -> L+delta. The other kind of destabilization mechanism is Zn diffused to the steel substrate by Fe2Al5 grain boundaries and directly produced 5 phase between Fe2Al5 and steel substrate interface, which caused outburst of Fe2Al5. The two kinds of Fe2Al5 destabilization mechanism are mutual coexistence and mutual competition, in particular conditions may be a mechanism to occupy absolute advantage.

Interface Reaction Dynamics and Mechanism of Plain Carbon Steel in Liquid Zinc

Study on the interface reaction layer of hydrogen reduction hot-rolled high-strength steel hot-dip galvanizing

Research on Corrosion Mechanism of Low Carbon Steel in Galvanizing Zinc

Interfacial Morphology and Corrosion Resistance of Fe–B Cast Steel Containing Chromium and Nickel in Liquid Zinc

Destabilization Mechanism of Fe-Al Inhibition Layer in Zn-0.2%Al Hot-Dip Galvanizing Coating and Related Thermodynamic Evaluation

Dissolution Mechanism of Solid Nickel in Liquid Zinc Saturated with Fe

Interfacial Reaction Between Solid Nickel and Liquid Zinc

Effect of Strip Entry Temperature on the Formation of Interfacial Layer During Hot-Dip Galvanizing of Press-Hardened Steel

Interfacial Morphology and Corrosion-Wear Behavior of Cast Fe-3.5 Wt.% B Steel in Liquid Zinc

Influence of Silicon on the Galvanized Coatings of Reactive Steels

Dissolution Mechanism of Solid Nickel in Liquid Zinc

Wetting of liquid Zinc-aluminum-magnesium alloy on steel substrate during hot-dipping: Understanding the role of the flux

Effect of Electrodeposited Ni Layer on the Galvanized Coatings of Reactive Steels

Microstructure and Corrosion Resistance of Zn-Al Diffusion Layer on 45 Steel Aided by Mechanical Energy

Understanding the Formation Mechanism of Al-Rich Interfacial Layer during Galvanizing of Cu Pre-coated High-Strength Steel Sheet

Growth Process and Mechanism of Hot-Dip Galvanised Zn–5Al Coating on Steel

Effect of solutes on the performance of Zn-coating and Zn-inducing transgranular cracking in steel based on DFT calculations

Mesoscale Investigation of Reaction–diffusion and Structure Evolution During Fe–Al Inhibition Layer Formation in Hot-Dip Galvanizing

Influence of silicon on the α-Fe/Γ interface of hot-dip galvanized steels

Study on Long-Term Hot Dipping Behavior of 316L Stainless Steel in Zn-5％Al Alloy Melt

Electrodeposition of decorative and protective Zn–Fe coating onto low-carbon steel substrate