Abstract:In this study, three cationic surfactants (hexadecyltrimethylammonium chloride, hexadecyldimethylbenzylammonium chloride, and octadecyltrimethylammonium chloride) were used to modify montmorillonite and polyethylene (PE)/maleic anhydride grafted polyethylene (PE-g-MAH)/organic-montmorillonite (Org-MMT) nano-composites, prepared by two blending processes (direct-melt blending and solution blending). X-ray diffractometry and transmission electron microscopy were used to investigate the intercalation behavior and microstructure of composites. Mechanical properties were also tested. It was found that the intercalation effect of PE/PE-g-MAH/Org-MMT could be enhanced by increasing the content of PE-g-MMT, using the silicate modified by a cationic surfactant with a benzyl group or long alkyl chain, adopting the solution-blending method or using high-density polyethylene as matrix. The degree of crystallinity of composites and the crystalline thickness perpendicular to the crystalline plane [like (110) and (200)] decreased with increasing amounts of PE-g-MAH and, under certain prescription, the crystalline thickness of the composite made by the solution method was much smaller than that made by direct-melt blending. This clearly showed that Org-MMT and PE-g-MAH had a heterogeneous nucleation effect on crystallization of PE from the melt, resulting in a decrease of crystalline thickness, and the heterogeneous nucleation effect was more evident in the nanocomposite made by the solution-blending method than in that made by the direct-melt intercalation process. The tensile strength initially increased and then decreased with increasing contents of PE-g-MAH. The maximum value in tensile strength (23.3 MPa) was achieved when the concentration of PE-g-MAH was 6 wt %. The impact strength increased concomitantly with the content of PE-g-MAH; it was 122.2 J/m when the concentration of PE-g-MAH was 9 wt %. (C) 2004 Wiley Periodicals, Inc.

Preparation of Montmorillonite Nanobelts Modified with Gluconic Acid

Preparation and characterization of organic modified montmorillonite/polylactic acid nanocomposites

In-situ Synthesis, Thermal and Mechanical Properties of Biobased Poly(ethylene 2,5-Furandicarboxylate)/montmorillonite (PEF/MMT) Nanocomposites

SWELLING BEHAVIOR OF MONTMORILLONITE, RHEOLOGICAL BEHAVIOR OF MONTMORILLONITE AQUEOUS SUSPENSION AND BLEND OF SUSPENSION AND EMULSION

Preparation and structure of poly(styrene-acrylonitrile)/montmorillonite nanocomposite

Preparation and Structure of Polystyrene/Montmorillonite Nanocomposite

Triglycidyl Para -Aminophenol Modified Montmorillonites for Epoxy Nanocomposites and Multi-Scale Carbon Fiber Reinforced Composites with Superior Mechanical Properties

Preparation and Properties of Polyurethane/Montmorillonite Nanocomposites Cured under Room Temperature

Wet Grinding of Montmorillonite and Its Effect on the Properties of Mesoporous Montmorillonite

Preparation and Properties of Organically Modified Na-Montmorillonite

Polyethylene/maleic Anhydride Grafted Polyethylene/organic‐montmorillonite Nanocomposites. I. Preparation, Microstructure, and Mechanical Properties

Effect of organophilic montmorillonite on polyurethane/montmorillonite nanocomposites

Renormalized linked-cluster expansion for strongly correlated lattice fermions in d=

Co-intercalation of Montmorillonite by Poly(oxypropylene) Amine Hydrochlorides with Different Chain Length

Preparation and Characterization of Nylon 66/montmorillonite Nanocomposites with Co-Treated Montmorillonites

Shrinkage Reduction in Nanopore-Rich Cement Paste Based on Facile Organic Modification of Montmorillonite

Preparation and properties of modified nano-montmorillonite viscosity reducers

Study on Sodium Montmorillonite Modified by Diallylmethyl Alkyl Ammonium Bromide

STRUCTURE AND MECHANICAL PROPERTIES OF NEWLY MODIFIED CLAY/EPOXY NANOCOMPOSITES PREPARED BY BALL MILLING

Preparation of montmorillonite nanocomposite and its adsorption

Preparation of Acid Activated Bentonite by Processing Couple Purification and Activation