STUDY ON PRUIFYING TECHNIQUE OF ATTAPULGITE

赖仕全,胡志孟,李同生

DOI: https://doi.org/10.16664/j.cnki.issn1008-0511.2003.05.003

2003-01-01

Abstract:Attapulgite was purified by mechanical stir and ultrasonic wave in order to improve its purity and enhance its dispersibility. The microscopic structures of attapulgite were studied by Scanning Electron Microscopy (SEM) and Transmission Electron Microscopy (TEM); TEM photos of attapulgite were treated with Image-Pro-Plus software in order to get distributions of its width and length; the thermal gravimetric analysis(TGA) of attapulgite was done by NETZSCH TG209 made in Germany. The experimental results showed that the purified attapulgite has less impurity, more thin and more short than the commercial attapulgite, its dispersion is more even. The length distribution of crude attapulgite is mostly 400～1000nm, the average is about 700nm, the width distribution is 10～35nm, the average is about 20nm,the length distribution of purified attapulgite is also 400～1000nm, the average is about 700nm, the width distribution is 5～30nm, the average is about 15nm, thus, distributions of length and width of the purified attapulgite are more narrow than that of the commercial attapulgite. It isn't different between thermal loss mass of purified attapulgite and that of commercial attapulgite, thermal loss mass curve has four obvious changes. when temperature reaches 780℃, its loss mass is about 17%.