Effect of Sr Modification on the Microstructures, Mechanical Properties, and Thermal Conductivity of Hypoeutectic Al-13.6Cu-6Si Alloys
Chengbo Li,Huibing Hou,Leilei Liu,Chengyi Huang,Yuelu Ren,Jun Du,Cailiu Yin
DOI: https://doi.org/10.1007/s11665-024-09752-5
IF: 2.3
2024-06-22
Journal of Materials Engineering and Performance
Abstract:The effects of Sr modification on the microstructure, mechanical properties, and thermal conductivity of the hypoeutectic Al-13.6Cu-6Si alloy were thoroughly investigated in the past using techniques such as optical microscopy, scanning electron microscopy, x-ray diffraction, cooling curve thermal analysis (CA-CCTA), universal testing machine, and laser thermal conductivity analyzer. The findings showed that the introduction of an appropriate amount of Sr into the alloy resulted in additional undercooling, enhancing the rate of non-uniform nucleation and significantly refining the α -Al grains. Furthermore, it effectively modified the morphology of eutectic silicon phases, transforming the plate-like structure into a fine and uniform coral-like appearance. Notably, the optimal modification effect was achieved with the addition of 0.3% Sr. Compared to the alloy without Sr modification, the secondary dendrite arm spacing of α -Al in the alloy was reduced from 14.26 to 9.23 μm. Additionally, the thermal conductivity, ultimate tensile strength, and elongation were significantly of the alloy increased to 130.1 W/(m K), 322 MPa, and 4.6%, respectively, representing an improvement of 10, 19, and 53%, respectively.
materials science, multidisciplinary