Effect of the Cr Content and Coiling Temperature on the Properties of Hot Rolled High Strength Lower Bainitic Steel

Lieven Bracke,Wei Xu

DOI: https://doi.org/10.2355/isijinternational.isijint-2015-086

2015-01-01

ISIJ International

Abstract:Hot rolled lower bainitic steels are suitable candidate materials for applications in which very high strength has to be combined with a certain degree of ductility. Typical applications include parts for trucks and trailers, heavy duty equipment and general mechanical engineering. To obtain suitable properties, an optimised combination of chemical composition and processing is required. For low alloyed C–Mn steels, Cr, Mo and B are typically added to suppress ferrite formation and increase bainitic hardenability during continuous cooling.1–5) In bainitic steels, Cr additions are typically less than 1 wt%5,6) to optimize the hardenability without compromising the welding behavior too much. B slows down the ferrite nucleation as it segregates to the austenite grain boundaries.7) Therefore, B is only effective as a hardening element when it is in solid solution, hence without formation of BN. This can be done by adding an element with a higher affinity for N, e.g. Ti.8) Mo is especially effective in increasing the hardenability when it is used together with B.9) Next to the chemical composition, the main processing parameters that determine the properties of the final hot rolled bainitic steel are the finish rolling temperature, the cooling rate and the coiling temperature.6) When rolling below the temperature of non-recrystallization (Tnr), deformation energy is stored in the austenite prior to cooling. This leads to a finer microstructure after transformation, which increases the strength.10) The stored energy, Effect of the Cr Content and Coiling Temperature on the Properties of Hot Rolled High Strength Lower Bainitic Steel