Low driving field-induced large strain in MnO2-modified 0.76Bi1/2Na1/2TiO3-0.24SrTiO3 lead-free piezoceramics
Xing-Ye Tong,Zong-Zheng Du,Yu-Ting Yang,Ming-Wei Song,Jia-Jun Zhou,Hai-Bin Zhang,Chun-Lin Guan,Hong Liu,Jing-Zhong Fang
DOI: https://doi.org/10.1016/j.jallcom.2020.158237
IF: 6.2
2021-03-01
Journal of Alloys and Compounds
Abstract:MnO2-modified 0.76Bi1/2Na1/2TiO3-0.24SrTiO3 (BNT-24ST) lead-free piezoceramics were synthesized by a conventional solid-state method. The introduction of MnO2 influences the phase structure and increases the grain size. Increasing the MnO2 content shifts the ferroelectric-relaxor transition temperature to below room temperature. This leads to a transition from ferroelectric behavior to ergodic-relaxor behavior. A large electrostrain of 0.18% and a normalized strain (S max /E max ) of 902 pm/V with an ultra-low driving field of 2 kV/mm are achieved for the 0.25 wt% MnO2 doped BNT-24ST. A temperature-insensitive S max /E max of above 610 pm/V from room temperature to 90 °C is achieved at 4 kV/mm. This is attributed to the modification by MnO2 and the low poling field. Excellent mechanical performance of Young’s modulus E~127.4 GPa and fracture toughness K IC ~1.38 MPa.m1/2 are also obtained, which are better than those reported for PZT-based ceramics. The results indicate the BNT-24ST with MnO2 ceramic is a promising candidate for piezoactuator applications.
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering