Preparation and enhanced electrical properties of grain-oriented (Bi 1/2 Na 1/2 )TiO 3 -based lead-free incipient piezoceramics

haibo zhang,peiwei xu,eric a patterson,jiadong zang,shenling jiang,jurgen rodel

DOI: https://doi.org/10.1016/j.jeurceramsoc.2015.03.012

IF: 5.7

2015-01-01

Journal of the European Ceramic Society

Abstract:(Bi1/2Na1/2)TiO3 (BNT) based lead-free incipient piezoceramics are promising candidates for actuator applications due to their giant electromechanical strains originating from the reversible relaxor-ferroelectric phase transition. To decrease the electric field required for this large strain, the templated grain growth method was employed to prepare 〈100〉 oriented 0.91Bi1/2Na1/2TiO3–0.06BaTiO3–0.03AgNbO3 piezoceramics using plate-like BNT templates. Textured samples provided a high unipolar strain of 0.38% and a corresponding large signal piezoelectric coefficient, d33∗ of 766pm/V at 5kV/mm, which are 78% higher than the values of the randomly oriented ones. The enhanced electric-field-induced strain at relatively lower field was attributed primarily to the facilitated phase-transition to form a long range ferroelectric order along the 〈100〉 direction. It was also found that the textured piezoceramics exhibited significantly reduced frequency dependence in the unipolar strain behavior at room temperature, resulting from the decreased electric field required for the relaxor-ferroelectric phase transition.