Abstract:Epoxy resin carbons are of high strength, high temperature resistance, and corrosion resistance, which are widely used as the precursor of carbon composite materials. However, the applications of epoxy resin carbons are greatly limited for the characteristic of non-graphitization and low char yield (22 wt%). In this paper, coal tar pitch was used to modify epoxy resin carbons via a simple heating mixing, pyrolysis and high temperature graphitization. The results show that the coal tar pitch content and heat treatment temperature can improve the ordered graphite carbon content. As the coal tar pitch content increase, the ordered graphite carbon content of modified epoxy resin carbon increase after 3000 °C graphitization for 0.5 h. Particularly, the graphitization degree of epoxy resin carbon and 40 wt% coal tar pitch modified epoxy resin carbon are 8.42 % and 44.21 %, respectively. The grain size (L c = 13.84 nm) and grain stacking height (L a = 7.79 nm) of 40 wt% coal tar pitch modified epoxy resin carbon are bigger than epoxy resin carbon (L c = 3.44 nm, L a = 3.45 nm). The ordered coal tar pitch graphite carbon and disordered epoxy resin amorphous carbon are evenly distributed in the modified epoxy resin carbon, indicating a good comparability of coal tar pitch and epoxy resin. Besides, the entangling carbon ribbon are observed in the epoxy resin carbon after graphitization at 3000 °C. With the increase of coal tar pitch content, the content of carbon element, aromatic ring number, the char yield and thermal decomposition temperature of modified epoxy resin increased. Moreover, the char yield of expoxy resion modified by 50 wt% coal tar pitch is 42 wt%, almost two times higher than that of epoxy resin (22 wt%). The increased char yield of modified epoxy resin mainly inherited the high char yield of coal tar pitch (50 wt%) and the chemical crosslinking weight gain. More interesting, the chemical crosslinking weight gain reaches the maximum value of 15 wt% when the content of coal tar pitch is 40wt%. The reason for that is the possible chemical crosslinking reaction can be occured by the epoxy group and hydroxyl group within epoxy resin and carboxyl group and phenolic hydroxyl group within coal tar pitch. This study provides some theory foundation for the future application of epoxy resin carbon composite materials.

Preparation and pyrolysis behavior of modified coal tar pitch as C/C composites matrix precursor

Study on the Variety of Rheological Properties and Thermal Analysis of Modified Coal Tar Pitch with 1,4-Benzenedimethanol

Pyrolysis mechanism of composite binder composed of coal tar pitch and phenolic resin for carbon materials

Effect of coal tar pitch modification on the structure and char yield of pyrolysis epoxy resin carbons

Analysis of the properties of two kinds of coal tar pitches used for impregnation of C/C composite

Enhancing spinnability and properties of carbon fibers through modification of isotropic coal tar pitch precursor

Preparation of pitch precursor with excellent spinnability for general-purpose carbon fibre using coal tar pitch as raw material

Preparation of mesocarbon microbeads from coal tar pitch with blending of biomass tar pitch

Further processing and prospect of coal tar pitch utilization

Mesophase formation of coal-tar pitches used for impregnant of C/C composites

Molecular representation and atomic-level coking evolution investigation of modified coal tar pitch via 13 C NMR, MALDI-TOF-MS, SAXS, and ReaxFF MD

Research on Coal Tar Pitch Catalytic Oxidation and Its Effect on the Emission of PAHs during Co-Carbonation with Coal

Modification of Coal Tar Pitch with Aromatic Nitro-Compounds

Preparation with different mixing ratios of anatase to activated carbon and their photocatalytic performance

Preparation and Characterization of Mesocarbon Microbeads by the Co-Polycondensation of High-Temperature Coal Tar Pitch and Coal Pyrolytic Extracts

Effect of coal tar pitch as carbon source on the electrochemical performance of silicon-carbon composites

De-agglomeration and homogenisation of nanoparticles in coal tar pitch-based carbon materials

Characterization of Composite Prepared with Different Mixing Ratios of TiO₂ to Activated Carbon and Their Photocatalytic Activity

Study on the characterization and thermal conversion behavior of sequential extraction products from medium temperature coal pitch

Cohesion and Toughness Improvement of Pitch Binder by Thermosetting Resin Modification for Tib2/C Composite Cathode

Changes in Functional Groups and Crystal Structure of Coal Tar Pitch with Respect to Carbonization Temperature