Abstract:Diphenyl carbonate (DPC) and diphenyl ketone (DPK) were used as diluents to prepare microporous polyvinylidene fluoride (PVDF) membranes via thermally induced phase-separation (TIPS) method. The liquid - liquid phase-separation phenomena were found in PVDF/DPC and PVDF/DPK systems during the thermally induced phase-separation processes. The monotectic points of PVDF/DPC and PVDF/DPK systems appeared at PVDF concentration approximately 30 and 56 %(wt), respectively. This suggested that PVDF membrane with a bicontinuous or cellular structure could be obtained when the PVDF concentration was less than the point values. The effects of polymer concentration and quenching temperature on the membrane structure, porosity, and tensile strength were also investigated. The results showed that low polymer concentration and high quenching temperature led to a large pore size membrane. The tensile strength of the membrane increased with the increase of the polymer concentration, but the porosity of the membrane decreased. On condition that the PVDF concentration was higher than monotectic points, only polymer crystallization occurred and a typical compact spherulitic structures were obtained. Moreover, a binary diluent of DPK and secondary solvent such as 1,2-propylene glycol (PG) was used to replace the single diluent in TIPS process. The phase diagram for the PVDF/binary diluent of DPK and PG system was measured in the range of the PG/DPK mass ratio changing from 0 to 2/3. Then the effects of the PG/DPK mass ratio and the PVDF concentration on membrane cross-section structures and tensile strength were also investigated. The results showed that the addition of PG brought about a shift of the cloud point curve to a higher temperature and the extension of the liquid-liquid phase separation region to a higher polymer concentration. Therefore a bicontinuous cross-section structure was obtained when the PG/DPK mass ratio was 3/7 and the polymer concentration was 30 wt%. As an increase of the PG/DPK mass ratio, the tensile strength increased gradually at a fixed PVDF concentration. Moreover, for the same PG/DPK mass ratio, the cross-section microstructure changed from a bicontinuous or a cellular structure to a spherulitic structure, and the tensile strength increased drastically as the polymer concentration increased from 20 wt% to 50 wt%. According to the properties of diluents, the industrial scale production line with a twin-screw extruder of microporous PVDF hollow fiber membranes was established and a series of different type hollow fiber membranes were prepared for the corresponding applications of pressure-driven modulus, submersed modulus and membrane bio-reactor modulus. At the same time, the full recycle of diluents was almostly actualized by using a series of unit opertaions such as extraction, distillation, delamination, sedimentation and drying processes. It means there is no waste emission in the preparation of PVDF membranes or it is a green process.

Preparation of Ectfe Membranes with Bicontinuous Structure Via Tips Method by A Binary Diluent

ECTFE Membranes Prepared Via Thermally Induced Phase Separation —selection of Mixed Diluent

Preparation of Porous PVDF Membrane Via Thermally Induced Phase Separation with Diluent Mixture of DBP and DEHP

Preparation of Ethylene Chlorotrifluoroethylene Co-polymer Membranes Via Thermally Induced Phase Separation

ECTFE Membrane Fabrication Via TIPS Method Using ATBC Diluent for Vacuum Membrane Distillation

Preparation of High Density Polyethylene/polyethylene- Block -Poly(ethylene Glycol) Copolymer Blend Porous Membranes Via Thermally Induced Phase Separation Process and Their Properties

Effect of Coagulation Bath Temperature on the Structure and Performance of Polyethersulfone Hollow Fiber Membranes by Dry/wet Process

The construction of an efficient magnesium-lithium separation thin film composite membrane with dual aqueous-phase monomers (PIP and MPD)

Preparation, Modification, and Application of Ethylene-Chlorotrifluoroethylene Copolymer Membranes

Green preparation of polyvinylidene fluoride microfiltration membranes via thermally indueced phase separation method using diphenyl carbonate and diphenyl ketone as diluents

Formation of a Bicontinuous Structure Membrane of Polyvinylidene Fluoride in Diphenyl Carbonate Diluent Via Thermally Induced Phase Separation

Preparation of non-woven supported ECTFE membrane by cast-coating method for membrane distillation

Wide Liquid-Liquid Phase Separation Region Enhancing Tensile Strength of Poly(vinylidene Fluoride) Membranes Via TIPS Method with a New Diluent

Poly(vinylidene fluoride) membrane preparation with an environmental diluent via thermally induced phase separation

Preparation and Characterization of Microporous PVDF Membrane by Thermally Induced Phase Separation from a Ternary Polymer/solvent/non-Solvent System

Preparation of PVDF Membranes via TIPS Method: The Effect of Mixed Diluents on Membrane Structure and Mechanical Property

The Effect of Diluent Mixture with Upper Critical Solution Temperature on Membrane Formation Process, Microstructure, and Performance of PVDF Hollow Fiber Membrane by TIPS Process

Structure formation and characterization of PVDF hollow fiber membrane prepared via TIPS with diluent mixture

Effects of Co-Diluent on the Pore Structure, Patterning Fidelity, and Properties of Membranes Fabricated by Lithographically Templated Thermally Induced Phase Separation

Phase Behavior of Polyetherimide/Benzophenone/Triethylene Glycol Ternary System and Its Application for the Preparation of Microporous Membranes

Preparation of microporous PVDF membrane via tips method using binary diluent of DPK and PG