Synthesis and properties of Ti-Al coating by high-frequency induction heated combustion
Chenggang Pan,Chengjie Fang,Ji Shi,Kaijiang Ma,Hui Yang,Peng He
DOI: https://doi.org/10.1016/j.jallcom.2023.168739
IF: 6.2
2023-01-12
Journal of Alloys and Compounds
Abstract:Ti-Al coatings with porosities of 1.11%− 2.28% were synthesized in situ via high-frequency induction heated combustion synthesis (HFIHCS) method within several minutes. The adiabatic temperatures at different preheating temperatures were calculated thermodynamically. The microstructure, phase composition, cross-sectional microhardness, oxidation, and corrosion resistance to molten aluminum alloy of the as-received coatings were investigated. The results showed that the Ti-Al reaction could be self-sustained when the preheating temperature reached 605 K. The combustion reaction and pore-forming mechanisms of the as-received Ti-Al coating conformed to liquid-solid reaction and thermal explosion, respectively. The coating microstructure followed a core-shell ring-shaped microstructure model, which was incomplete Ti nuclei, Ti 3 Al, TiAl and TiAl 2 phases from inside to outside. The average microhardness of the substrate, interface and coating were 508.57, 454.54 and 377.18 HV 0.2 , respectively. The microhardness fluctuation was the largest at the coating-substrate interface. The oxidation kinetics of the as-received coating approximately followed a linear rate law with an oxidation rate constant of 0.3943 mg·cm −2 ·h −1 and a rate exponent of 1.2372. The oxide layer consisted of an outer layer of TiO 2 , an inner layer of nitrogen-containing compounds and a mixed layer of TiO 2 and Al 2 O 3 between them. The corrosion mechanism of the as-received Ti-Al IMC coatings in molten A380 alloy was mainly controlled by the combination of compounds formed at the liquid-solid interface and diffusion of liquid metal into the as-received Ti-Al coating, rather than by the dissolution mechanism of the as-received Ti-Al coating.
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering