Improving oxidation resistance of γ-TiAl based alloy by depositing TiAlSiN coating: Effects of silicon
Kai Zhang,Li Xin,Yiliang Lu,Yuxian Cheng,Xiaolan Wang,Shenglong Zhu,Fuhui Wang
DOI: https://doi.org/10.1016/j.corsci.2020.109151
IF: 7.72
2021-02-01
Corrosion Science
Abstract:<p>To improve oxidation resistance of γ-TiAl based alloys, Ti<sub>0.5</sub>Al<sub>0.4</sub>Si<sub>0.1</sub>N coating was deposited on Ti48Al2Cr2Nb alloy by arc ion plating system. Ti<sub>0.5</sub>Al<sub>0.5</sub>N coating was also deposited for comparison. TiAlSiN coating exhibited excellent cyclic oxidation resistance at 900 °C mainly due to Si promoted selective oxidation of Al and formation of a continuous Al<sub>2</sub>O<sub>3</sub> top layer in oxide scale. Another beneficial effect of Si is promoting in situ formation of Ti<sub>5</sub>Si<sub>3</sub> diffusion barrier layer at coating/substrate interface during thermal exposure, which inhibited interdiffusion between coating and alloy, especially nitrogen inward diffusion in alloy and helped the coating maintaining long term oxidation resistance.</p>
materials science, multidisciplinary,metallurgy & metallurgical engineering