Abstract:It is irrefutable that the presence of hydrogen reduces the mechanical performance of many metals and alloys used for structural components. Several mechanisms of hydrogen-assisted cracking (HAC) of steels have been postulated. The direct evidence of the mechanisms by which hydrogen embrittles these materials has remained elusive. This is by virtue of our difficulty to directly observe the hydrogen distribution at spatial resolutions less than 100 nm and analysis volumes greater than 1 × 109 atoms at microstructural features such as grain boundaries, dislocations, twins, stacking faults and sub-micron inclusions that are all potential hydrogen trapping sites postulated to be responsible for the degradation of mechanical performance. Here, we report on an experimental methodology combining an elaborate fatigue testing protocol in an enriched gaseous deuterium environment with NanoSIMS (secondary ion mass spectrometry) imaging for detection of deuterium at spatial resolutions as low as 100 nm and accompanying TEM analysis. Type 316 stainless steel compact tension specimens were precharged in deuterium followed by fatigue testing at high stress ratio (0.7), low delta K (~11 MPa √m), and a frequency of 1 cycle per minute using a sawtooth waveform with a rise time of 30 s in high pressure (68.9 MPa) gaseous deuterium (99.999% purity) environment at room temperature. High resolution NanoSIMS imaging was then used to measure the deuterium distribution at the tip of and in the wake of secondary and tertiary fatigue cracks as well as at MnS inclusions. The use of deuterium eliminates the difficulties of interpreting hydrogen measurements by SIMS relating to the ubiquitous presence of hydrogen in all high vacuum systems and guarantees that deuterium measured by the NanoSIMS must be attributed to the fatigue testing protocol. This methodology has allowed us to directly observe the distribution of hydrogen in dislocation tangles ahead and in the wake of fatigue crack tips and at the interface of MnS inclusions. The protocol provides an avenue by which the path and speed with which hydrogen proceeds along its embrittling course of action may be directly followed through modifications of the fatigue testing parameters and/or alloy type and allows a means to validate at least qualitatively recently published models of enhanced hydrogen transport by dislocations.

An apparatus for detecting hydrogen desorption from metals during deformation

Hydrogen Desorption from 6061 Aluminum Alloy During Deformation Detected by a New Apparatus

Hydrogen Environment Fatigue Test System Development of High Pressure Hydrogen Storage Vessels

Research on Hydrogen Environment Fatigue Test System and Correlative Fatigue Test of Hydrogen Storage Vessel

Testing Machine for Testing Durability of Material under High-Pressure Hydrogen Circumstance

The finding of hydrogen trapping at phase boundary in austenitic stainless steel by scanning Kelvin probe force microscopy

High resolution NanoSIMS imaging of deuterium distributions in 316 stainless steel specimens after fatigue testing in high pressure deuterium environment

Apparatus for material tests using an internal loading system in high-pressure gas at room temperature

Design of PC Based High Pressure Hydrogen Absorption/desorption Apparatus

Hydrogen and deuterium charging of lifted-out specimens for atom probe tomography

Experimental study of the hydrogen-microstructure interactions in a pre-strained 316L austenitic stainless steel

Hydrogen Effect on the Deformation Evolution Process in Situ Detected by Nanoindentation Continuous Stiffness Measurement

Solute hydrogen and deuterium observed at the near atomic scale in high-strength steel

Analysis of Hydrogen Distribution and Diffusion in Pre-Strained SUS316L through Scanning Kelvin Probe Force Microscopy and Thermal Desorption Spectroscopy

Hydrogen and deuterium charging of site-specific specimen for atom probe tomography

Observation of hydrogen diffusion channel and hydrogen trap in 304 austenitic stainless steel

Analysis of hydrogen-induced delayed cracking and hydrogen trapping behavior in plastically deformed quenching and partitioning steel

An investigation of the mechanical behaviour of hydrogen storage metal beds on hydriding and dehydriding and several methods of preventing the damage of hydride containers caused by the expansion of hydrogen storage metals

Probing hydrogen content in steel using the thermoelectric effect

Development of a System for Fast Measuring Hydrogen Content in Aluminum Alloy Melt Based on Dynamic Measurement of Hydrogen Partial Pressure

Effect of plastic deformation at room temperature on hydrogen diffusion of S30408