Interrelationship between hydrogen and α′-martensite of SUS 304 austenitic stainless steel revealed by tensile tests
Hui-yun Zhang,Liu-wei Zheng,Tao Wang,Wen-jie Lv,Quan-xin Shi,Jin-yao Ma,Yi Luo,Wei Liang,Jun Hu,R.D.K. Misra
DOI: https://doi.org/10.1016/j.msea.2021.142169
2022-01-01
Abstract:The hydrogen embrittlement (HE) behavior on SUS 304 austenitic stainless steel (ASS) was investigated by in-situ scanning electron microscope(SEM)observations combined with electron backscatter diffraction (EBSD), slow strain rate tensile (SSRT) tests and nanoindentation techniques. The specimens for in-situ tensile tests were cathodic pre-charged with hydrogen for 0 and 96 h, and the in-situ EBSD and SEM indicated that α′-martensite was generated along the twin boundaries during the tensile process of 304 ASS, and the pre-charged hydrogen promoted the α′-martensite transformation. In turn, the tensile sample was first stretched by 20% to produce α′-martensite and then hydrogen charged, and the SSRT tests showed that the pre-existing α′-martensite increases the hydrogen diffusion depth and HE sensitivity of the experimental steels. The results of nanoindentation experiments showed that hydrogen was captured by the grain boundary as hydrogen trap, which slightly reduced the average hardness of the material, but the role of hydrogen in hardness cannot be overestimated. The presence of α′-martensite in 304 ASS determined the fracture mechanism during the subsequent tensile process. If the sample had no α′-martensite at the time of hydrogen charging, the fracture mode was transgranular fracture with the cracks initiating and propagating along the twin boundaries. But when the sample contained a certain amount of α′-martensite when hydrogen charging was carried out, the fracture mode was intergranular fracture with cracks initiating along the twin boundaries but propagating along the grain boundaries.
materials science, multidisciplinary,nanoscience & nanotechnology,metallurgy & metallurgical engineering