Crystal Growth and Luminescent Properties of ZnO Sub-microrods Prepared by One Step Solution Growth Method
CHEN Jian-gang,GUO Chang-xin,ZHANG Lin-li,HU Jun-tao
DOI: https://doi.org/10.3321/j.issn:1000-7032.2006.01.011
2006-01-01
Chinese Journal of Luminescence
Abstract:ZnO hexagonal sub-microrods have been synthesized onto glass substrates through aqueous growth method by using the thermal decomposition of an aqueous solution of equimolar zinc nitrate(Zn(NO_3)_2·4H_2O) or zinc acetate(Zn(CH_3COO)_2·2H_2O))with methenamine ((CH_2)_6N_4) by controlling the experimental conditions. XRD patterns, SEM images have been measured, which reveals the shape of the most of the ZnO sub-microrods are hexagonal-rod with two flat faces on the two ends, but some are pair rods symmetrically grown from a center to both sides and some form radial clusters from one center. The length of the rods is from 5 μm to 8 μm, the diameter from 300 nm to 700 nm and the ratio of the length to the diameter is more than 10∶1. When the growth time reaches 48 h, we found that the microrods turned into hollow microtubes with the tube-thickness in the tenth of diameter. The growth mechanism is discussed by using the growth model of cathodion ligand tetrahedron. Zn-(NO_3)_2 dissolves and forms growth units of tetrahedron Zn-(OH)_4 under the reaction of the surface activator (CH_2)_6N_4. Then the incorporation of growth units leads to the formation of the ZnO crystal lattice at the interface through a dehydration reaction (OH~-+ OH~-H_2O+O~ 2- ). The fastest of the growth speed along 0001- direction leads to the formation of the ZnO microrods. The reason of forming hollow microtubes is the face of (0001) and 0001- of ZnO rods as eroded by chemical dissolution because of its metastable state. The excitation spectra of ZnO sub-microrods show that except the intrinsic inter-band excitation shorter than 370 nm, there is a strong exciton excitation peak located at around 377~385 nm at room temperature. The photoluminescent spectra show that there is a wide orange-red emission peaking at about 630 nm and FWHM 250 nm with the excitation wavelength 310 nm. When the excitation is a strong 325 nm He-Cd laser, the same sample will emit a strong excition emission peaking at about 385 nm, with FWHM 16 nm and a green emission peaking at about 552 nm with FWHM 120 nm. Compared with the calculated data of these intrinsic defects with the theory of FP-LMTO, the green, orange-red and red emission peaks can be attributed to the transition of oxygen vacancies to the valence band. The studies on PL of ZnO sub-microrods after annealing showed that the excitation peak at about 384 nm disappeared, and the orange-red defect emission (peak at ~630 nm) shows red shift (peak at ~710 nm), and the emission intensity increases. The excitation spectra of samples after annealing showed an enhanced exciton peak at ~377 nm. It indicates that after annealing, the energy transfer from the excition to the defect center occurred.