Abstract:In this work, we studied the microstructure and mechanical properties of hot-pressed B4C, B4C + 5 wt% TiAl, and B4C + B + 5 wt% TiAl. The X-ray diffraction and Raman spectroscopy results showed that the addition of Ti–Al alone did not led to Al doping in B4C, and it did not reduce the degree of amorphization of B4C generated under high shear stresses. In contrast, the co-addition of Ti–Al and B resulted in both B and Al solid solutions in the B4C and effectively mitigated the amorphization of B4C. Electron probe microanalysis (EPMA) and energy dispersive X-ray spectroscopy (EDS) analyses suggested that the co-addition of Ti–Al and B promoted the interdiffusion of lightweight elements such as B, C, Al, Mg, and Si at high temperatures, resulting in a dense body with uniformly distributed second phase. The transmission electron microscopy (TEM) observations of the B4C + B + 5 wt% TiAl sample showed that a nano–core–shell structure with aggregated dislocations in the shells which was generated at TiB2 grains due to the segregation and dissolution-precipitation between TiB2 and B-rich boron carbide. The short-range ordered substitution of B and the disordered doping of Al in B4C led to lattice distortion and expansion, resulting in the formation of high-density defects, including stacking faults and nano-twins, improving the mechanical properties for B4C. The B4C + B + 5 wt% TiAl sample exhibits a combination of fascinating properties, including low density (2.52 g/cm3), high Vickers hardness (35.53 ± 0.83 GPa) and moderate fracture toughness (4.37 ± 0.35 MPa m1/2).

Transient Liquid Phase Spark Plasma Sintering of B4C-based Ceramics Using Ti-Al Intermetallics As Sintering Aid

Microstructure and mechanical properties of B4C based ceramics with Fe3Al as sintering aid by spark plasma sintering

Toughening mechanism of B4C/TiB2 ceramic materials by in situ reaction via spark plasma sintering

Microstructure and mechanical behaviour of transient liquid phase spark plasma sintered B4C–SiC–TiB2 composites from a B4C–TiSi2 system

Mechanical properties and pre-oxidation behavior of spark plasma sintered B4C ceramics using (Ti3SiC2+CeO2/La2O3) as sintering aid

Enhancement mechanical properties of in-situ preparated B4C-based composites with small amount of (Ti3SiC2+Si)

Effect of Ti and its compounds on the mechanical properties and microstructure of B4C ceramics fabricated via pressureless sintering

Microstructures and mechanical properties of TiB2 composite ceramics with co-addition of Ti and TiC fabricated by SPS

The effect of B and Ti–Al intermetallics additions on the microstructure and mechanical properties of hot-pressed B4C

B4C-based hard and tough ceramics densified via spark plasma sintering using a novel Mg2Si sintering aid

In-situ synthesis and low-temperature fabrication of B4C/TiB2-based multilayer graded composites with B4C and Ti–Al intermetallics mixtures through transient liquid phase sintering

Influence of Y2O3 contents on sintering and mechanical properties of B4C-Al2O3 multiphase ceramic composites

B4C‒TiB2 composite with modified microstructure and enhanced properties from optimal size coupling of raw powders

Effects of Boron Content on the Microstructure and Properties of BxC-TiB2 (x=4.5, 6.5 or 8.5) Ceramic Composites by the Reactive Spark Plasma Sintering

Effects of TiB2 Particles on the Microstructure Evolution and Mechanical Properties of B4C/TiB2 Ceramic Composite

Microstructure and mechanical properties of TiB2–B4C ceramics fabricated by hot-pressing

The Effect of CNTs on the Spark Plasma Sintering Densification Behavior and Mechanical Properties of B4C-Si Powders

β→α Phase Transformation and Properties of Solid-State-Sintered SiC Ceramics with TaC Addition

Effect of Ti Doping on the Mechanical Properties of B4C Composite Ceramics

Densification and strengthening mechanism in spark plasma sintering of B4C–VB2 ceramics via carbide boronizing

Integrated preparation of B4C–TiB2 multilayer graded ceramics with high hardness and high toughness