Abstract:Layered double hydroxide (LDH) films have attracted extensive attention in Mg alloy anti-corrosion due to their unique physical barrier function and ion exchange performance. However, most of the LDH films on Mg alloy have problems of harsh preparation conditions, poor anti-corrosion stability, and poor adhesion. In this paper, a typical Li–Al-alanine (Ala) LDH film has been successfully prepared on AZ91D Mg alloy surface under milder conditions using multi-arc ion plating and in-situ dipping for the first time. Then an improved vacuum impregnation further modified the Li–Al-Ala LDH film in an ethanol solution of stearic acid (SA) to improve its protective stability. The potentiodynamic polarization curves and electrochemical impedance spectra (EIS) showed that the Li–Al-Ala LDH/SA film's corrosion resistance is more than three orders of magnitude higher than that of the blank Mg alloy in 3.5 wt% NaCl, showing a highly increased corrosion resistance. The long-term immersion experiments found that the surface structure and corrosion resistance of the Li–Al-Ala LDH/SA film did not change much after immersion in 3.5 wt% NaCl for 432 h. The bonding force between the film and the Mg alloy substrate can reach grade 0 based on the standard from International Standardization Organization (ISO). And the hydrophobicity of the film can remain stable with the water contact angle (WCA) being steady at about 140° after a certain distance of external abrasion, showing excellent mechanical wear resistance. The study provides a new milder approach to fabricating superhydrophobic LDH films with durable anti-corrosion resistance, good adhesion, and mechanical stability on Mg alloy surface.

Wetting Behavior and Drag Reduction of Superhydrophobic Layered Double Hydroxides Films on Aluminum

Preparation and Wettability of Zn–Al Layered Double Hydroxide Film Directly Grown on Highly Porous Anodic Alumina Oxide Template

Wettability and Drag Reduction of A Superhydrophobic Aluminum Surface

Facile Fabrication and Properties of Super-hydrophobic MgAl-LDH Films With Excellent Corrosion Resistance on AZ31 Magnesium Alloy

Drag-reductive and Anti-Corrosive Superhydrophobic Surface Fabricated on Aluminum with Thin PDMS/SiO2coating

Facile fabrication and evaluation of self-healing Zn-Al layered double hydroxide superhydrophobic coating on aluminum alloy

Fabrication of Superhydrophobic Surface with Different Metal Films on Aluminum Alloy

Ni-Al Layered Double Hydroxides (ldhs) Coated Superhydrophobic Mesh with Flower-Like Hierarchical Structure for Oil/water Separation

Fabrication of Superhydrophobic Aluminum Surface by Droplet Etching and Chemical Modification

Preparation of superhydrophobic Li–Al-Ala LDH/SA film with enhanced corrosion resistance and mechanical stability on AZ91D Mg alloy

Facile and Fast Fabrication Method for Mechanically Robust Superhydrophobic Surface on Aluminum Foil

Fabrication of Stable Superhydrophobic Surface with Low Adhesion on Aluminum Foil

Fabrication of Aluminum Superhydrophobic Surface with Facile Chemical Etching Method

In Situ One-Step Fabrication of Superhydrophobic Layered Double Hydroxide on Al Alloys for Anti-Corrosion

A simple fabrication method for mechanically robust superhydrophobic surface by hierarchical aluminum hydroxide structures

A green one-step fabrication of superhydrophobic metallic surfaces of aluminum and zinc

Superhydrophobic surfaces created by a one-step solution-immersion process and their drag-reduction effect on water

Development of superhydrophobic layered double hydroxide directly on zinc substrate: structural and corrosion resistance properties

Study on the Dray Reduction of the Superhydrophobic Surface

Spray-coated Superhydrophobic Surfaces with Wear-Resistance, Drag-Reduction and Anti-Corrosion Properties

Fabrication and drag reduction of superhydrophobic surface on steel substrates