Fabrication of Superhydrophobic Aluminum Surface by Droplet Etching and Chemical Modification

Xin Zhang,Jing Zhao,Jiliang Mo,Ruoyu Sun,Zhen Li,Zhiguang Guo
DOI: https://doi.org/10.1016/j.colsurfa.2019.01.046
IF: 5.518
2019-01-01
Colloids and Surfaces A Physicochemical and Engineering Aspects
Abstract:The development of techniques to fabricate superhydrophobic aluminum surfaces is rapidly maturing, yet the problems of high loss of material and complex preparation still persist. To address this, a simple method that combines droplet etching and chemical modification was used to fabricate a superhydrophobic aluminum surface, with a contact angle of 156 degrees and a sliding angle of 5 degrees. Compared with the traditional immersion method, droplet etching can properly preserve the integrity of the aluminum material and also provide a rough structure on the aluminum surface. The optimal superhydrophobicity of the aluminum surface was obtained by one-step immersion in pentadecafluorooctanoic acid aqueous solution at 80 degrees C. Thermostability, anticorrosion, self-cleaning, and antifouling tests were subsequently performed. The results demonstrated that the superhydrophobic aluminum surface was easily prepared and possessed thermostability, anticorrosion, self-cleaning and antifouling abilities.
What problem does this paper attempt to address?