Abstract:A series of nitrogen-doped carbons were prepared by using biomass waste sawdust as carbon source for supercapacitors. A new nitrogen-doping strategy was proposed to introduce nitrogen element into carbons by using ethylenediamine and carbon as nitrogen source through the polymerization reaction on sawdust under moderate conditions. The raw carbons were further activated with KOH to improve the surface area to increase the electric double layer capacitance while the heteroatoms can improve the pseudocapacitance. The prepared carbons were characterized with different techniques and the electrochemical performances were tested. It was found that the nitrogen-doped carbons activated with a KOH to carbon mass ratio of 5 (NC600-800-5) has the largest specific surface area (1674 m(2)g(-1)) and moderate nitrogen content (2.88 wt%). Compared with the carbon without introduction of nitrogen element (C600-800-5), the capacitive performances of nitrogen-doped carbons were greatly improved, which may be due to the increase of pseudocapacitance and the improvement of wettability introduced by nitrogen element. The largest specific capacitance, 367 F g(-1), was reached at 0.5 A g(-1 )in 6 M KOH solution while the specific capacitance of C600-800-5 is only 279 F g(-1). After 10,000 cycles at 3 A g(-1), the specific capacitance can keep 96.7% of the initial value, suggesting the excellent cycling performance. The energy density can reach 8.7 Wh Kg(-1) at a power density of 251.6 W kg(-1). Thus, it is proved that the nitrogendoping strategy is effective and the introduction of nitrogen element to carbons is particularly important to the improvement of the electrochemical performances.

Preparation of N-, S-Co-Doped Activated Carbons Derived from Waste Medium Density Fiberboard for Supercapacitors

N-doped Carbons with Hierarchically Micro- and Mesoporous Structure Derived from Sawdust for High Performance Supercapacitors

Nitrogen-functionalized Microporous Carbon Nanoparticles for High Performance Supercapacitor Electrode

Cooking Carbon with Protic Salt: Nitrogen and Sulfur Self-Doped Porous Carbon Nanosheets for Supercapacitors

Preparation of Nitrogen-containing Activated Carbon from Waste Medium Density Fiberboard for Electric Double Layer Capacitor

Preparation of Inexpensive S-doped Porous Carbons for High-Performance Supercapacitors

Nitrogen- and Sulfur-Doped Carbon Obtained from Direct Hydrothermal Carbonization of Cellulose and Ammonium Sulfate for Supercapacitor Applications

N,S‐Co‐Doped Activated Carbon Prepared by a Thiourea‐Assisted "Cutting" Method and their Application as High‐Performance Supercapacitors

Thiocyanogen-modulated N, S Co-doped lignin hierarchical porous carbons for high-performance aqueous supercapacitors

N-doped Hierarchically Micro- and Mesoporous Carbons with Superior Performance in Supercapacitors

N-Doped Porous Carbons with High Surface Areas Prepared Through One-Step Chemical Activation and Their Application for Supercapacitors

Nitrogen-Doped Porous Carbons Through Koh Activation with Superior Performance in Supercapacitors

An environmentally friendly process to derive N/O/S-codoped porous carbon from biomass waste with high yield for high performance supercapacitor

Nitrogen and Sulfur Codoped Porous Carbon Directly Derived from Potassium Citrate and Thiourea for High-Performance Supercapacitors.

N/O co-doped porous carbon synthesized by lewis acid salt activation for high rate performance supercapacitor

Nitrogen-doped porous carbon derived from biomass waste for high-performance supercapacitor

High-surface-area and high-nitrogen-content carbon microspheres prepared by a pre-oxidation and mild KOH activation for superior supercapacitor

Pore-structure Regulation and Heteroatom Doping of Activated Carbon for Supercapacitors with Excellent Rate Performance and Power Density

Hydrothermal Carbonization of Cellulose with Ammonium Sulfate and Thiourea for the Production of Supercapacitor Carbon

Novel Nitrogen‐Doped Porous Carbon with High Surface Areas Prepared from Industrial Alkali Lignin for Supercapacitors

Preparation of a N-P co-doped waste cotton fabric-based activated carbon for supercapacitor electrodes