Abstract:To enhance the toughness of metallic glasses (MGs), considerable scientific efforts have been made to investigate the physical mechanism of fracture behavior of MGs in past few years. However, many unresolved puzzles remain about the fracture mechanisms of MGs at present. In this paper, Molecular Dynamics (MD) simulations have been used to investigate the tensile fracture behavior of Al based MGs under nine different Engineering strain rates. Our results show that the higher the Engineering strain rate is, the longer the period of plastic deformation, the shorter the crack length. we have observed that Al amorphous with notch gradually crystallizes during tensile fracture, however, there are differences in the degree of crystallization and atomic arrangement as well as micro-structure in different regions with different Engineering strain rates. In the process of tensile fracture of Al based MGs, the crack propagation mainly along the hexagonal-close-packed (HCP) grain boundaries between face-centered-cubic (FCC) crystal blocks. As the Engineering strain increases, numerous HCP atoms located at grain boundaries gradually migrate into the interior of FCC crystal blocks, the velocity of crack propagation will also increase and finally induce the brittle fracture of Al based MGs. Meanwhile, we effectively demonstrated the existence of HCP and FCC atoms in Al based MGs during tensile deformation by analyzing the bond-orientational order parameters q l . The analysis of thermodynamics (entropy) showed that there is a positive correlation between the Engineering strain rate and the strain of maximum entropy when the Engineering strain rate exceeds 0.002 ps -1 . The formation of cavitation ahead of crack could be attributed to the migrate of atoms from the higher entropy cavity region to the lower entropy crystallization region. This study enriches the traditional tensile deformation theories and provides a new understanding for the physical origins of cavitation in the crack tip of MGs.

Mechanical Behavior of Micronanoscaled Metallic Glasses

Atomistic Origin of Size Effects in Fatigue Behavior of Metallic Glasses

Failure behavior and criteria of metallic glasses

Fatigue of Metallic Glasses

Cyclic Deformation in Metallic Glasses.

Strain-hardening and failure mechanisms of metallic glasses under triaxial stress

Uniform Tensile Elongation in Framed Submicron Metallic Glass Specimen in the Limit of Suppressed Shear Banding

Strength Softening at Shear Bands in Metallic Glasses

Size Effects on Tensile and Compressive Strengths in Metallic Glass Nanowires

Shear Band Control for Improved Strength-Ductility Synergy in Metallic Glasses

Inverse size effects in un-notched and notched metallic glass thin films

Strengthening Mechanisms in Nanoporous Metallic Glasses

Anisotropic and Size-Dependent Mechanical Responses of Free-Standing Ni-Nb Metallic Glass Thin Film

Shear Band Evolution under Cyclic Loading and Fatigue Property in Metallic Glasses: A Brief Review

Deformation Behavior of Metallic Glasses with Shear Band Like Atomic Structure: a Molecular Dynamics Study.

Atomistic Investigation of Mechanical Properties of Metallic Glass Nanocomposites

In Situ Micromechanical Characterization of Metallic Glass Microwires under Torsional Loading

Microstructural mechanisms of tuning the deformation behaviors in annealed metallic glasses

Hierarchical micro-nanostructured Zr-based metallic glass with tensile plasticity

Mechanical Behavior of Metallic Glasses: Microscopic Understanding of Strength and Ductility

The influence of Engineering strain rates on the atomic structure, crack propagation and cavitation formation in Al based metallic glass