Effect of an Aryl Amide Derivative on the Crystallization Behaviour and Impact Toughness of Poly(Ethylene Terephthalate)

Zhiyuan Shen,Faliang Luo,Qian Xing,Pengfei Si,Xiaomei Lei,Lijie Ji,Shengfang Ding,Kezhi Wang
DOI: https://doi.org/10.1039/c6ce00114a
IF: 3.756
2016-01-01
CrystEngComm
Abstract:Poly(ethylene terephthalate) (PET) and aryl amide derivative (TMB-5) blends were prepared by melt blending. It was found that TMB-5 shows a significant nucleation effect on PET and especially the nonisothermal nucleation efficiency reached up to 80.7% at a very low content of 0.6 wt% TMB-5. The effects of TMB-5 on the crystallization behavior and mechanical properties of PET were systematically investigated. DSC results show that crystallization temperature of PET apparently increased by nearly 20 degrees C with the addition of 0.6 wt% TMB-5 during the cooling process. A remarkable acceleration in the crystallization rate of PET was achieved as analyzed using the Avrami equation. Wide angle X-ray diffraction (WAXD) and polarized optical microscopy (POM) results show that the addition of TMB-5 remarkably increases the crystallinity and nuclei density of PET. Small angle X-ray scattering (SAXS) measurements reveal that the long period of PET decreased and lamellar thickness increased with an increase in TMB-5 content. The impact strength of PET was greatly enhanced by the addition of TMB-5, and a toughening mechanism was proposed.
What problem does this paper attempt to address?