Recovery Strategy and Mechanism of Aged Lithium Ion Batteries after Shallow Depth of Discharge at Elevated Temperature.

Yingzhi Cui,Chunyu Du,Yunzhi Gao,Jie Yang,Lingling Zhang,Ting Guan,Lijie Yang,Xinqun Cheng,Pengjian Zuo,Yulin Ma,Geping Yin

DOI: https://doi.org/10.1021/acsami.5b10474

IF: 9.5

2016-01-01

ACS Applied Materials & Interfaces

Abstract:Performance degradation of prismatic lithium ion batteries (LIBs) with LiCoO2 and mesocarbon microbead as active materials is investigated at an elevated temperature for shallow depth of discharge. Aged LIBs are disassembled to characterize the interface morphology, bulk structure, and reversible capacity of an individual electrode. It is found that the formation of interfacial blocking layer (IBL) on the anode results in the cathode state of charge (SOC) offset, which is the primary reason for the cathode degradation. The main capacity degradation of the anode is attributed to the IBL on the anode surface that impedes the intercalation and deintercalation of lithium ions. Because the full battery capacity is limited by the cathode during aging, the cathode SOC offset is the most important reason for the full battery capacity loss. Interestingly, the capacity of aged LIBs can be recovered to a relative high level after adding the electrolyte, rather than the solvent. This recovery is attributed to the rel...